'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC Makrolon® 6487 700314 COVESTRO SHANGHAI
78
- Unit Price:US$ 3,153 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:50MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Easy to process｜High impact resistance｜Flame retardant｜Medium viscosity
- Application Areas:household electrical appliances｜Plastic barrel｜Medical Supplies｜Electrical applications｜Automotive Applications｜building
- Color:--
- Grade:Injection grade
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak | |
| Charpy Notched Impact Strength | 23°C,Partial Break | ISO 7391 | 70 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C,Complete Break | ISO 7391 | 12 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO 6603-2 | 6000 | N |
| Multi axis Instrumented Impact Energy | 23°C | ISO 6603-2 | 50.0 | J |
| -30°C | ISO 6603-2 | 55.0 | J | |
| Impact strength of cantilever beam gap | 23°C,Partial Break | ISO 7391 | 65 | kJ/m² |
| Multi axis Instrumented Peak Impact Force | 23°C | ISO 6603-2 | 5200 | N |
| Charpy Notched Impact Strength | -30°C,Complete Break | ISO 7391 | 12 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| ApplicationofFlamefromSmallBurner MethodKandF | 2.00mm | DIN 53438-1,-3 | K1.F1 | |
| Extreme Oxygen Index | ISO 4589-2 | 36 | % | |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 930 | °C |
| Burning rate - US-FMVSS | >1.00mm | ISO 3795 | passed | |
| UL flame retardant rating | 3.0mm | UL 94 | 5VA | |
| 1.5mm | UL 94 | V-0 | ||
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 960 | °C |
| 3.0mm | IEC 60695-2-12 | 960 | °C | |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 900 | °C |
| FlashIgnitionTemperature | ASTM D1929 | 470 | °C | |
| SelfIgnition | ASTM D1929 | 550 | °C | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| tensile strength | Break,23°C | ISO 527-2/50 | 65.0 | Mpa |
| Yield,23°C | ISO 527-2/50 | 66.0 | Mpa | |
| Tensile modulus | 23°C | ISO 527-2/1 | 2450 | Mpa |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | >50 | % |
| Bending modulus | 23°C | ISO 178 | 2450 | Mpa |
| bending strength | 3.5%Strain,23°C | ISO 178 | 75.0 | Mpa |
| 23°C | ISO 178 | 99.0 | Mpa | |
| Bending strain | 23°C | ISO 178 | 7.0 | % |
| Tensile strain | Yield,23°C | ISO 527-2/50 | 6.0 | % |
| Break,23°C | ISO 527-2/50 | 120 | % | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| RTI Str | 1.5mm | UL 746 | 125 | °C |
| RTI Imp | 1.5mm | UL 746 | 115 | °C |
| thermal conductivity | 23°C | ISO 8302 | 0.20 | W/m/K |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 6.5E-05 | cm/cm/°C |
| RTI Elec | 1.5mm | UL 746 | 125 | °C |
| Vicat softening temperature | -- | ISO 306/B50 | 143 | °C |
| -- | ISO 306/B120 | 141 | °C | |
| Ball Pressure Test | 135°C | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO 11359-2 | 6.5E-05 | cm/cm/°C |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO 75-2/B | 134 | °C |
| 1.8MPa,Unannealed | ISO 75-2/A | 122 | °C | |
| Glass transition temperature | ISO 11357-2 | 141 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 0.12 | % |
| Shrinkage rate | TD | ISO 2577 | 0.60-0.80 | % |
| MD | ISO 2577 | 0.60-0.80 | % | |
| TD:2.00mm3 | ISO 294-4 | 0.75 | % | |
| MD:2.00mm3 | ISO 294-4 | 0.70 | % | |
| Water absorption rate | Saturation,23°C | ISO 62 | 0.30 | % |
| Apparent density | ISO 60 | 0.64 | g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 10 | g/10min |
| Melt Volume Flow Rate (MVR) | 300°C/1.2kg | ISO 1133 | 9.00 | cm3/10min |
| density | 23°C | ISO 1183 | 1.20 | g/cm³ |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Volume resistivity | 23°C | IEC 60093 | 1E+16 | ohms·cm |
| Surface resistivity | IEC 60093 | 1E+16 | ohms | |
| Relative permittivity | 23°C,100Hz | IEC 60250 | 3.10 | |
| Dielectric strength | 23°C,1.00mm | IEC 60243-1 | 34 | KV/mm |
| Dissipation factor | 23°C,100Hz | IEC 60250 | 8E-04 | |
| Relative permittivity | 23°C,1MHz | IEC 60250 | 3.00 | |
| Dissipation factor | 23°C,1MHz | IEC 60250 | 9E-03 | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Ball Pressure Test | ISO 2039-1 | 117 | Mpa | |
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| Electrolytic corrosion | 23°C | IEC 60426 | A1 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.