PC/ABS CYCOLOY™ CX7240-701 SABIC INNOVATIVE NANSHA
333
- Unit Price:US$ 5,896 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:135MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜High impact resistance｜High mobility
- Application Areas:Electrical field｜Electronic field｜Architectural application field｜Outdoor applications｜Engine hood parts｜Medical supplies｜Nursing supplies｜Plastic bag｜Casters｜Aerospace Applications｜Liquid handling
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 100 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 89.0 °C | |
| 1.8MPa,未退火,6.40mm | ASTM D648 | 99.0 °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 93.0 °C | |
| vicat | ASTM D152512 | 110 °C | |
| -- | ISO 306/B50 | 110 °C | |
| -- | ISO 306/B120 | 113 °C | |
| ball-indentation hardness | 75°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 7.5E-05 cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C | |
| TD：-40到40°C | ISO 11359-2 | 7.5E-05 cm/cm/°C | |
| thermal conductivity | ISO 8302 | 0.20 W/m/K | |
| RTI Elec | UL 746 | 90.0 °C | |
| RTI Imp | UL 746 | 90.0 °C | |
| RTI Str | UL 746 | 90.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 800 °C |
| Limiting Oxygen Index | ISO 4589-2 | 35 % | |
| UL flame retardant rating | 0.60mm | UL 94 | V-1 |
| 0.75mm | UL 94 | V-0 | |
| 1.5mm | UL 94 | 5VB | |
| 3.0mm | UL 94 | 5VA | |
| Burning wire flammability index | 0.75mm13 | IEC 60695-2-12 | 960 °C |
| 0.75mm | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | 0.75mm13 | IEC 60695-2-13 | 775 °C |
| 1.0mm | IEC 60695-2-13 | 825 °C | |
| 1.5mm13 | IEC 60695-2-13 | 775 °C | |
| 3.0mm13 | IEC 60695-2-13 | 775 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C7 | ISO 179/1eA | 10 kJ/m² |
| 23°C8 | ISO 179/1eA | 22 kJ/m² | |
| 23°C7 | ISO 179/1eA | 20 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 180 J/m |
| 23°C | ASTM D256 | 700 J/m | |
| -30°C9 | ISO 180/1A | 10 kJ/m² | |
| -30°C10 | ISO 180/1A | 10 kJ/m² | |
| 23°C9 | ISO 180/1A | 25 kJ/m² | |
| 23°C10 | ISO 180/1A | 20 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 65.0 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 饱和,23°C | ISO 62 | 0.20 % |
| 平衡,23°C,50%RH | ISO 62 | 0.10 % | |
| density | ASTM D792 | 1.19 g/cm³ | |
| ISO 1183 | 1.20 g/cm³ | ||
| melt mass-flow rate | 260°C/2.16kg | ASTM D1238 | 18 g/10min |
| Melt volume flow rate | 260°C/2.16kg | ISO 1133 | 15.0 cm3/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.60 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 35 KV/mm |
| 1.60mm,在油中 | IEC 60243-1 | 25 KV/mm | |
| 3.20mm,在油中 | IEC 60243-1 | 17 KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2600 Mpa | |
| ISO 527-2/1 | 2600 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 65.0 Mpa |
| 屈服 | ISO 527-2/50 | 65.0 Mpa | |
| 断裂 | ASTM D638 | 58.0 Mpa | |
| 断裂 | ISO 527-2/50 | 50.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 4.1 % |
| Tensile strain | 屈服 | ISO 527-2/50 | 4.0 % |
| elongation | 断裂 | ASTM D638 | 100 % |
| Tensile strain | 断裂 | ISO 527-2/50 | 90 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2500 Mpa |
| ISO 178 | 2500 Mpa | ||
| bending strength | ISO 178 | 96.0 Mpa | |
| 屈服,50.0mm跨距 | ASTM D790 | 104 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.