POM KEPITAL® FS2022 KEP KOREA
254
- Unit Price:US$ 3,741 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:58MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:wear resistant
- Application Areas:--
- Color:--
- Grade:Wear resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 10 g/10min | |
| ISO 1133 | 8.6 cm²/10min | ||
| ASTM D-1238 | 10 g/10min | ||
| Water absorption rate | ASTM D-570 | 0.22 % | |
| Shrinkage rate | 2.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | ASTM D-790 | 2.50×10 Kgf/cm | |
| elongation at break | ASTM D-732 | 540 Kgf/cm | |
| Impact strength of cantilever beam gap | ASTM D-256 | 6.5 Kgf.cm/cm | |
| tensile strength | ASTM D-638 | 560 Kgf/cm | |
| bending strength | ASTM D-790 | 780 Kgf/cm | |
| Rockwell hardness | ASTM D-785 | 80 M | |
| elongation | ASTM D-638 | 85 % | |
| Impact strength of cantilever beam gap | ASTM D-1822 | 105 Kgf.cm/cm |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ASTM D-257 | 1×10 Ω.cm | |
| Surface Resistivity | ASTM D-257 | 1×10 Ω |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | IS075 | 150 ℃ | |
| IS075 | 100 ℃ | ||
| melting temperature | ISO 11357 | 166 ℃ | |
| ISO 11359 | 1.1E-4 cm/cm/"C | ||
| ISO 11359 | 1.1E-4 cm/cm/℃ | ||
| UL flame retardant rating | UL -94 | HB | |
| Hot deformation temperature (HDT) | ASTM D-648 | 110 °C | |
| melting temperature | DSC Method | 165 °C | |
| Hot deformation temperature (HDT) | ASTM D-648 | 150 °C | |
| Linear expansion coefficient | ASTM D-696 | 13×10 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.