PBT Cristin® SK603 BK851 DUPONT USA
195
- Unit Price:US$ 3,769 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜Filler: Glass fiber reinforced material｜Good strength (glass fiber reinforced｜20% by weight ratio)｜20% filler by weight
- Application Areas:Automotive Applications｜Electronic and electrical components｜Industrial applications｜Automotive Applications
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO 306/B50 | 210 °C | |
| melting temperature | ISO 11357-3 | 224 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 4E-05 cm/cm/°C |
| TD | ISO 11359-2 | 1E-04 cm/cm/°C | |
| 平行流动方向，23 to 55℃(73 to 130°F) | ISO 11359-1 | 0.000100 cm/cm/℃ | |
| 垂直流动方向，23 to 55℃(73 to 130°F) | ISO 11359-1 | 0.000040 cm/cm/℃ | |
| Heat Deflection Temperature | 0.45 Mpa，未退火 | ISO 75B-1 | 220 ℃ |
| 1.80 Mpa，未退火 | ISO 75B-1 | 204 ℃ | |
| UL flame retardant rating | 0.750 mm | UL 94 | HB |
| 1.50 mm | UL 94 | HB | |
| 3.00 mm | UL 94 | HB | |
| melting temperature | ISO 3146 | 225 ℃ | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 220 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 204 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 1.00mm | ISO 3795 | 28 mm/min |
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 1.5mm | UL 94 | HB | |
| 0.75mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| Limiting Oxygen Index | ISO 4589-2 | 19 % | |
| FMVSS flammability | FMVSS302 | B | |
| Fogging-G-value | condensate)4 | ISO 6452 | 1E-04 g |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Emissions of Organic Compounds | VDA277 | 140 µgC/g | |
| Odor | VDA270 | 3.00 |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-1 | 19 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 9.0 kJ/m² |
| 23°C | ISO 179/1eA | 8.0 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 55 kJ/m² |
| 23°C | ISO 179/1eU | 60 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.0 kJ/m² |
| 23°C | ISO 180/1A | 9.0 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 60 kJ/m² |
| 23°C | ISO 180/1U | 60 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1E+15 ohms | |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 29 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 4.00 |
| 1MHz | IEC 60250 | 3.60 | |
| Dissipation Factor | 100Hz | IEC 60250 | 1.2E-03 |
| 1MHz | IEC 60250 | 0.019 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ThermalConductivityofMelt | 0.25 W/m/K | ||
| Water absorption rate | 23C/59RH | ISO 62 | 0.15 % |
| Sat/23C | ISO 62 | 0.4 % | |
| shrinkage rate | Across Flow | ISO 294-4 | 1.0 % |
| Flow | ISO 294-4 | 0.35 % | |
| density | ISO 1183 | 1.45 g/cm | |
| MediumDensity | 1.26 g/cm³ | ||
| Ejection Temperature | 170 °C | ||
| SpecificHeatCapacity of Melt | 1860 J/kg/°C | ||
| density | ISO 1183 | 1.45 g/cm³ | |
| shrinkage rate | TD | ISO 294-4 | 1.1 % |
| MD | ISO 294-4 | 0.30 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.40 % |
| 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.15 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23℃, Type 1, Edgewise, Notch A | ISO 179 | 7.5 KJ/m |
| Tensile stress | 23℃，断裂 | ISO 527-1 | 120 MPa |
| Tensile strain | 23℃，断裂 | ISO 527-1 | 3.2 % |
| Tensile modulus | 23℃ | ISO 527-1 | 7400 MPa |
| flexural modulus | 23℃ | ISO 178 | 6200 MPa |
| bending strength | 23℃ | ISO 178 | 180 MPa |
| Suspended wall beam without notch impact strength | 23 ℃, Type 1 | ISO 180 | 44 KJ/m |
| Impact strength of cantilever beam gap | 23 ℃, Type 1, Notch A | ISO 180 | 8 KJ/m |
| Tensile creep modulus | 1h | ISO 899-1 | 7200 MPa |
| 1000h | ISO 899-1 | 5600 MPa | |
| Impact strength of simply supported beam without notch | -30℃, Type 1, Edgewise | ISO 179 | 54 KJ/m |
| 23 ℃, Type 1, Edgewise | ISO 179 | 56 KJ/m | |
| Charpy Notched Impact Strength | -30 ℃, Type 1, Edgewise, Notch A | ISO 179 | 9.8 KJ/m |
| flexural modulus | ISO 178 | 6500 Mpa | |
| bending strength | ISO 178 | 180 Mpa | |
| Tensile modulus | ISO 527-2 | 7000 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 120 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 3.2 % |
| Tensile creep modulus | 1hr | ISO 899-1 | 7200 Mpa |
| 1000hr | ISO 899-1 | 5600 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.