TPEE

TPEE Hytrel® 3078 DUPONT USA

439

Unit Price:US$ 8,522 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:UV resistance｜Thermal stability
Application Areas:Automotive Applications｜Electrical applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak

flammability	Test Condition	Test Method	Test Result
Burning rate	1.00mm	ISO 3795	<100 mm/min
UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	3.0mm	UL 94	HB
		UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	3.0mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index		ISO 4589-2	19 %
FMVSS flammability		FMVSS302	B

elastomer	Test Condition	Test Method	Test Result
tear strength	横向Flow	ISO 34-1	77 kN/m
tear strength	tear strength	Flow	ISO 34-1	80 kN/m

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	24.0 Mpa
tensile strength	Break	ISO 527-2	24.0 Mpa
	tensile strength	10%Strain	ISO 527-2	1.80 Mpa
	tensile strength	tensile strength	50%Strain	ISO 527-2	5.00 Mpa
Tensile strain	Break	ISO 527-2	>300 %
Nominal tensile fracture strain		ISO 527-2	900 %
Tensile creep modulus	1hr	ISO 899-1	22.0 Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	18.0 Mpa
Bending modulus		ISO 178	21.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Brittle temperature		ISO 974	-98.0 °C
Glass transition temperature		ISO 11357-2	-60.0 °C
Melting temperature		ISO 11357-3	177 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.8E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	2.1E-04 cm/cm/°C
Effective thermal diffusivity coefficient			5.44E-08 m²/s

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	190°C/2.16kg	ISO 1133	5.0 g/10min
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	5.00 cm3/10min
Shrinkage rate	TD	ISO 294-4	0.60 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.60 %
Water absorption rate	23°C,24hr	ISO 62	0.50 %
	Water absorption rate	Saturation,23°C,2.00mm	ISO 62	0.80 %
	Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.20 %
MediumDensity			0.940 g/cm³
SpecificHeatCapacity of Melt			2150 J/kg/°C
ThermalConductivityofMelt			0.15 W/m/K

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	1MHz	IEC 60250	0.015
Surface resistivity		IEC 60093	1E+14 ohms
Volume resistivity		IEC 60093	1E+13 ohms·cm
Dielectric strength		IEC 60243-1	18 KV/mm
Relative permittivity	100Hz	IEC 60250	5.40
Relative permittivity	Relative permittivity	1MHz	IEC 60250	5.30
Dissipation factor	100Hz	IEC 60250	7E-03

hardness	Test Condition	Test Method	Test Result
Shore hardness	ShoreD	ISO 868	30
Shore hardness	Shore hardness	ShoreD,15Sec	ISO 868	26

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

TPEE Hytrel® 3078 DUPONT USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet