Material Properties:enhance｜toughness｜copolymer｜medial｜Balanced｜rigidity｜Filler: Glass fiber reinforced material｜15% filler by weight
Application Areas:Automotive Applications｜pipeline
Color:--
Grade:Injection grade

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	1.8MPa,未退火	ASTM D648	130 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,未退火	ISO 75-2/A	159 °C
melting temperature		ASTM D3418	165 °C
melting temperature	melting temperature		ISO 11357-3	166 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	4.6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1E-04 cm/cm/°C

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	4.9 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.3 kJ/m²

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	1.54 g/cm³
density	density		ISO 1183	1.50 g/cm³
shrinkage rate	MD	ASTM D955	0.40 %
	shrinkage rate	TD	ASTM D955	1.8 %
		shrinkage rate	TD	ISO 294-4	0.90 %
		shrinkage rate	shrinkage rate	MD	ISO 294-4	0.50 %
Water absorption rate	饱和,23°C	ISO 62	0.80 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.20 %

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	断裂	ISO 527-2/1A/5	91.0 Mpa
Tensile strain	断裂	ISO 527-2/1A/5	2.5 %
flexural modulus	23°C	ISO 178	5850 Mpa
Tensile modulus		ISO 527-2/1A/1	5950 Mpa
tensile strength	屈服,23°C	ASTM D638	85.5 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.