PC Makrolon® 8035 COVESTRO GERMANY

408

Unit Price:US$ 3,678 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
26MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜enhance｜Filler: Glass fiber with embossing｜30% filler by weight
Application Areas:Electrical field｜Electronic field｜Fiber grade
Color:--
Grade:Enhanced level

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C,CompleteBreak	ISO 7391	8.0	kJ/m²
Impact strength of simply supported beam without notch	-60°C,CompleteBreak	ISO 179/1eU	45	kJ/m²
	Impact strength of simply supported beam without notch	-30°C,Complete Break	ISO 179/1eU	45	kJ/m²
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C,Complete Break	ISO 179/1eU	40	kJ/m²
Impact strength of cantilever beam gap	23°C,CompleteBreak	ISO 7391	8.0	kJ/m²
Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	5.00	J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	5.00	J
Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	800	N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	1300	N
flammability	Test Condition	Test Method	Test Result	Test Unit
Hot filament ignition temperature	0.75mm	IEC 60695-2-13	875	°C
Burning wire flammability index	3.0mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	1.5mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	Burning wire flammability index	0.75mm	IEC 60695-2-12	960	°C
UL flame retardant rating	1.5mm	UL 94	V-1
SelfIgnition		ASTM D1929	550	°C
Needle flame test	MethodK:3.00mm	IEC 60695-11-5	2.0	min
	Needle flame test	MethodK:2.00mm	IEC 60695-11-5	1.0	min
		Needle flame test	MethodK:1.50mm	IEC 60695-11-5	1.0	min
			Needle flame test	MethodF:3.00mm	IEC 60695-11-5	2.0	min
				Needle flame test	MethodF:2.00mm	IEC 60695-11-5	2.0	min
				Needle flame test	Needle flame test	MethodF:1.50mm	IEC 60695-11-5	2.0	min
Burning rate - US-FMVSS	>1.00mm	ISO 3795	passed
FlashIgnitionTemperature		ASTM D1929	470	°C
Hot filament ignition temperature	1.5mm	IEC 60695-2-13	875	°C
Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	875	°C
Extreme Oxygen Index		ISO 4589-2	37	%
ApplicationofFlamefromSmallBurner MethodKandF	2.00mm	DIN 53438-1,-3	K1.F1
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Break,23°C	ISO 527-2/5	3.5	%
Tensile creep modulus	1hr	ISO 899-1	4700	Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	3900	Mpa
Bending modulus	23°C	ISO 178	4700	Mpa
Tensile strain	Yield,23°C	ISO 527-2/50	2.5	%
tensile strength	Break,23°C	ISO 527-2/5	55.0	Mpa
bending strength	3.5%Strain,23°C	ISO 178	100	Mpa
bending strength	bending strength	23°C	ISO 178	105	Mpa
Bending strain	23°C	ISO 178	4.5	%
Tensile modulus	23°C	ISO 527-2/1	5100	Mpa
tensile strength	Yield,23°C	ISO 527-2/50	59.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ISO 306/B50	147	°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	141	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	135	°C
Vicat softening temperature	--	ISO 306/B120	148	°C
Ball Pressure Test	137°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	3.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	5.5E-05	cm/cm/°C
thermal conductivity	23°C	ISO 8302	0.24	W/m/K
RTI Elec	1.5mm	UL 746	125	°C
RTI Imp	1.5mm	UL 746	115	°C
RTI Str	1.5mm	UL 746	125	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Apparent density		ISO 60	0.69	g/cm³
density	23°C	ISO 1183	1.42	g/cm³
melt mass-flow rate	300°C/1.2kg	ISO 1133	5.0	g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	4.00	cm3/10min
Shrinkage rate	TD	ISO 2577	0.25-0.40	%
	Shrinkage rate	MD	ISO 2577	0.25-0.40	%
		Shrinkage rate	TD:2.00mm3	ISO 294-4	0.35	%
		Shrinkage rate	Shrinkage rate	MD:2.00mm3	ISO 294-4	0.50	%
Water absorption rate	Saturation,23°C	ISO 62	0.22	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.10	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	23°C,1MHz	IEC 60250	9E-03
Dissipation factor	Dissipation factor	23°C,100Hz	IEC 60250	1.5E-03
Relative permittivity	23°C,1MHz	IEC 60250	3.50
Relative permittivity	Relative permittivity	23°C,100Hz	IEC 60250	3.50
Dielectric strength	23°C,1.00mm	IEC 60243-1	36	KV/mm
Volume resistivity	23°C	IEC 60093	1E+16	ohms·cm
Surface resistivity		IEC 60093	1E+16	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	149	Mpa
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Electrolytic corrosion	23°C	IEC 60426	A1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.