PEI ULTEM™ 1010-5173 SABIC INNOVATIVE US

206

Unit Price:US$ 22,808 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜transparent｜enhance｜Flame retardant
Application Areas:Food service sector
Color:--
Grade:--

Technical Data Sheet Compare

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M 级	ASTM D785	109

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa, 未退火, 6.40 mm	ASTM D648	207 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, 未退火, 6.40 mm	ASTM D648	198 °C
vicat		ASTM D15255	218 °C
Linear coefficient of thermal expansion	-20 到 150°C，流动	ASTM E831	5.6E-5 cm/cm/°C
thermal conductivity		ASTM C177	0.22 W/m/K
RTI Elec		UL 746	170 °C
RTI Imp		UL 746	170 °C
RTI		UL 746	170 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA
Limiting Oxygen Index		ASTM D2863	44 %

Impact resistance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ASTM D4812	1300 J/m
Reverse notch impact	3.20 mm	ASTM D256	1200 J/m
Dart impact	23°C	ASTM D3029	33.0 J

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	337°C/6.6 kg	ASTM D1238	18 g/10 min
shrinkage rate	3.20 mm，Flow	内部方法	0.50 - 0.70 %
Water absorption rate	24 hr	ASTM D570	0.25 %
Water absorption rate	Water absorption rate	平衡, 23°C	ASTM D570	1.3 %

Electrical performance	Test Condition	Test Method	Test Result
volume resistivity		ASTM D257	1.0E+17 ohms·cm
dielectric strength	1.60 mm, in Air	ASTM D149	33 KV/mm
dielectric strength	dielectric strength	1.60 mm, in Oil	ASTM D149	28 KV/mm
dielectric constant	1 kHz	ASTM D150	3.15
Dissipation Factor	1 kHz	ASTM D150	1.3E-3
Dissipation Factor	Dissipation Factor	2.45 GHz	ASTM D150	2.5E-3
arc resistance		ASTM D495	PLC 5
Compared to the Leakage Tracking Index (CTI)		UL 746	PLC 4
High arc combustion index (HAI)		UL 746	PLC 3
High Voltage Arc Traceability Rate (HVTR)		UL 746	PLC 2
Hot wire ignition (HWI)		UL 746	PLC 1

injection	Test Condition	Test Method	Test Result
drying temperature			150 °C
drying time			4.0 to 6.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 60 %
Temperature at the rear of the barrel			330 to 400 °C
Temperature in the middle of the barrel			340 to 400 °C
Temperature at the front of the material cylinder			345 to 400 °C
Spray nozzle temperature			345 to 400 °C
Processing (melt) temperature			350 to 400 °C
mold temperature			135 to 165 °C
Back pressure			0.300 to 0.700 Mpa
screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	3580 Mpa
tensile strength	屈服	ASTM D638	110 Mpa
elongation	屈服	ASTM D638	7.0 %
elongation	elongation	断裂	ASTM D638	60 %
flexural modulus	100 mm 跨距	ASTM D790	3510 Mpa
bending strength	屈服, 100 mm 跨距	ASTM D790	165 Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 转轮	ASTM D1044	10.0 mg

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.