PC Makrolon® 1803 550645 COVESTRO SHANGHAI
200
- Unit Price:US$ 8,115 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:26MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Thermal stability｜enhance｜High temperature resistance｜high viscosity
- Application Areas:Automotive sector｜Laptop case｜Electrical field｜Electronic field
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 121 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 159 °C |
| vicat | ISO 306/B120 | 184 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 174 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| RTI Elec | UL 746 | 150 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI Str | UL 746 | 150 °C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ISO 489 | 1.573 | |
| transmissivity | 1000µm | ISO 13468-2 | 89.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | 25 % | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Burning wire flammability index | IEC 60695-2-12 | 850 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| electrolytic corrosion | 23°C | IEC 60426 | A1 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 饱和,23°C | ISO 62 | 0.30 % |
| 平衡,23°C,50%RH | ISO 62 | 0.12 % | |
| Melt volume flow rate | 330°C/2.16kg | ISO 1133 | 10.0 cm3/10min |
| shrinkage rate | TD:2.00mm | ISO 294-4 | 0.85 % |
| MD:2.00mm | ISO 294-4 | 0.85 % | |
| density | 23°C | ISO 1183 | 1.15 g/cm³ |
| melt mass-flow rate | 330°C/2.16kg | ISO 1133 | 10 g/10min |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 8E-03 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 1 |
| 解决方案B | IEC 60112 | PLC 4 | |
| relative permittivity | 23°C,100Hz | IEC 60250 | 2.90 |
| 23°C,1MHz | IEC 60250 | 2.80 | |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 1E-03 |
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| volume resistivity | 23°C | IEC 60093 | 1E+17 ohms·cm |
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 35 KV/mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | 屈服,23°C | ISO 527-2/50 | 6.8 % |
| Tensile modulus | 23°C | ISO 527-2/1 | 2400 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2/50 | 72.0 Mpa |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | >50 % |
| flexural modulus | 23°C | ISO 178 | 2400 Mpa |
| bending strength | 23°C | ISO 178 | 108 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.