PC Makrolon® AL2447 COVESTRO SHANGHAI

332

Unit Price:US$ 2,194 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
64MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜Flame retardant
Application Areas:Automotive Applications｜Casters
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
Refractive index		ISO 489	1.586
transmissivity	1000μm	ISO 13468-2	89.0 %
	transmissivity	2000μm	ISO 13468-2	89.0 %
		transmissivity	3000μm	ISO 13468-2	88.0 %
		transmissivity	transmissivity	4000μm	ISO 13468-2	>87.0 %
turbidity	3000μm	ISO 14782	<0.50 %

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	-30°C,Complete Break	ISO 7391	15 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,Partial Break	ISO 7391	65 kJ/m²
Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	65.0 J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	55.0 J
Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	6000 N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	5100 N
Charpy Notched Impact Strength	-30°C,Complete Break	ISO 7391	14 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C,Partial Break	ISO 7391	65 kJ/m²
Impact strength of simply supported beam without notch	-60°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂

flammability	Test Condition	Test Method	Test Result
Extreme Oxygen Index		ISO 4589-2	28 %
FlashIgnitionTemperature		ASTM D1929	480 °C
SelfIgnition		ASTM D1929	550 °C
UL flame retardant rating	2.7mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	0.75mm	UL 94	V-2

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ISO 527-2/1	2400 Mpa
tensile strength	Yield,23°C	ISO 527-2/50	66.0 Mpa
	tensile strength	Break,23°C	ISO 527-2/5	70.0 Mpa
	tensile strength	tensile strength	Break,23°C	ISO 527-2/50	65.0 Mpa
Tensile strain	Yield,23°C	ISO 527-2/50	6.0 %
	Tensile strain	Break,23°C	ISO 527-2/5	130 %
	Tensile strain	Tensile strain	Break,23°C	ISO 527-2/50	120 %
Nominal tensile fracture strain	23°C	ISO 527-2/50	>50 %
Tensile creep modulus	1hr	ISO 899-1	2200 Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	1900 Mpa
Bending modulus	23°C	ISO 178	2350 Mpa
bending strength	23°C	ISO 178	98.0 Mpa
bending strength	bending strength	3.5%Strain,23°C	ISO 178	74.0 Mpa
Bending strain	23°C	ISO 178	7.0 %

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	138 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	125 °C
Glass transition temperature		ISO 11357-2	145 °C
Vicat softening temperature	--	ISO 306/B50	144 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	145 °C
Ball Pressure Test	135°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	MD:23to55°C	ISO 11359-2	6.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to55°C	ISO 11359-2	6.5E-05 cm/cm/°C
thermal conductivity	23°C	ISO 8302	0.20 W/m/K
RTI Elec	1.5mm	UL 746	125 °C
RTI Imp	1.5mm	UL 746	115 °C
RTI	1.5mm	UL 746	125 °C

Physical properties	Test Condition	Test Method	Test Result
Apparent density		ISO 60	0.66 g/cm³
melt mass-flow rate	300°C/1.2kg	ISO 1133	20 g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	19.0 cm3/10min
Shrinkage rate	TD	ISO 2577	0.50-0.70 %
	Shrinkage rate	MD	ISO 2577	0.50-0.70 %
		Shrinkage rate	TD:2.00mm4	ISO 294-4	0.70 %
		Shrinkage rate	Shrinkage rate	MD:2.00mm4	ISO 294-4	0.65 %
Water absorption rate	Saturation,23°C	ISO 62	0.30 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.12 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1E+16 ohms
Volume resistivity	23°C	IEC 60093	1E+16 ohms·cm
Dielectric strength	23°C,1.00mm	IEC 60243-1	34 KV/mm
Relative permittivity	23°C,100Hz	IEC 60250	3.10
Relative permittivity	Relative permittivity	23°C,1MHz	IEC 60250	3.00
Dissipation factor	23°C,100Hz	IEC 60250	5E-04
Dissipation factor	Dissipation factor	23°C,1MHz	IEC 60250	9E-03
Compared to the anti leakage trace index	SolutionA	IEC 60112	V
Compared to the anti leakage trace index	Compared to the anti leakage trace index	SolutionB	IEC 60112	V

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test		ISO 2039-1	115 Mpa

film	Test Condition	Test Method	Test Result
Water vapor permeability	23°C,85%RH,100μm	ISO 15106-1	15 g/m²/24hr
GasPermeation	CarbonDioxide:23°C,25.4μm	ISO 2556	18900 cm³/m²/bar/24hr
	GasPermeation	CarbonDioxide:23°C,100.0μm	ISO 2556	4800 cm³/m²/bar/24hr
		GasPermeation	Nitrogen:23°C,25.4μm	ISO 2556	630 cm³/m²/bar/24hr
			GasPermeation	Nitrogen:23°C,100.0μm	ISO 2556	160 cm³/m²/bar/24hr
				GasPermeation	Oxygen:23°C,25.4μm	ISO 2556	3150 cm³/m²/bar/24hr
				GasPermeation	GasPermeation	Oxygen:23°C,100.0μm	ISO 2556	800 cm³/m²/bar/24hr

Supplementary Information	Test Condition	Test Method	Test Result
Electrolytic corrosion	23°C	IEC 60426	A1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC Makrolon® AL2447 COVESTRO SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet