PA6

PA6 Durethan® BKV140H2.0 900051 LANXESS GERMANY

225

Unit Price:US$ 2,871 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
57.8MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			抗冲击热稳定性

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	100 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	110 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	90 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	90 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638/ISO 527	11200 kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	174 kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	10400 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	280 kg/cm²(MPa)[Lb/in²]
bending strength	bending strength	FlexuralStrainatFlexuralStrength5(23°C)		4.2 %
Tensile modulus	23°C	ISO 527-2/1	12000 Mpa
tensile strength	Break,23°C	ISO 527-2/5	185 Mpa
Tensile strain	Break,23°C	ISO 527-2/5	3.4 %
Bending modulus	23°C	ISO 178/A	11000 Mpa
bending strength	3.5%Strain	ISO 178/A	280 Mpa
bending strength	bending strength	23°C	ISO 178	290 Mpa

thermal performance	Test Condition	Test Method	Test Result
Combustibility (rate)		UL 94	HB
Vicat softening temperature		ASTM D1525/ISO R306	200 ℃（℉）
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	217 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	201 °C
Melting temperature		ISO 11357-3	220 °C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.46
Shrinkage rate	TD:280°C,2.00mm2	ISO 294-4	0.75 %
	Shrinkage rate	TD:120°C,2hr,2.00mm3	ISO 294-4	0.090 %
		Shrinkage rate	MD:280°C,2.00mm2	ISO 294-4	0.21 %
		Shrinkage rate	Shrinkage rate	MD:120°C,2hr,2.00mm3	ISO 294-4	0.070 %

Supplementary Information	Test Condition	Test Method	Test Result
ISO Shortcut		ISO 1874	PA6HI.GR.14-120.GF40

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 Durethan® BKV140H2.0 900051 LANXESS GERMANY

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet