ABS

ABS POLYLAC® PA-726M ZHENJIANG CHIMEI

411

Unit Price:US$ 1,600 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
164MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:High gloss｜Easy electroplating
Application Areas:Automotive sector
Color:--
Grade:Injection grade

Material Certification

MSDS

SGS

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	22 kJ/m²
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	230 J/m
	Impact strength of cantilever beam gap	23°C	ISO 180/1A	20 kJ/m²
		Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	210 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	9.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength	--6	ISO 178	63.0 Mpa
bending strength	bending strength	--5	ASTM D790	61.6 Mpa
Bending modulus	--6	ISO 178	2100 Mpa
Bending modulus	Bending modulus	--5	ASTM D790	2070 Mpa
elongation	Break	ISO 527-2/50	20 %
elongation	elongation	Break4	ASTM D638	35 %
tensile strength	Break	ISO 527-2/50	32.0 Mpa
	tensile strength	Yield	ISO 527-2/50	42.0 Mpa
	tensile strength	tensile strength	Yield4	ASTM D638	39.6 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD	ISO 11359-2	8.7E-05 cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	95.0 °C
Vicat softening temperature	Vicat softening temperature	--	ASTMD15257	103 °C
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	96.0 °C
	Hot deformation temperature	1.8MPa,Annealed	ASTM D648	94.0 °C
		Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	81.0 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	84.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate		ISO 294-4	0.40-0.70 %
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	23.0 cm3/10min
melt mass-flow rate	200°C/5.0kg	ASTM D1238	2.0 g/10min
density	23°C	ISO 1183	1.04 g/cm³
density	density	--3	ASTM D792	1.04 g/cm³

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	112

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.