Material Properties:enhance｜Thermal stability
Application Areas:Industrial applications｜Automotive sector｜Electric｜Electronic application field｜Fasteners｜Laptop case｜Application in the automotive field
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00mm	FMVSS302	<100	mm/min
UL flame retardant rating	1.6mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1	2500	Mpa
tensile strength	Yield	ISO 527-2/50	67.0	Mpa
Tensile strain	Yield	ISO 527-2/50	4.3	%
Tensile strain	Tensile strain	Break	ISO 527-2/50	30	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	194	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	60.0	°C
Melting temperature		DIN EN11357-1	260	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	275°C/5.0kg	ISO 1133	55.0	cm3/10min
Hygroscopicity	70°C，62%RH	ISO 1110	2.5	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.