ABS TAIRILAC® AF3538 FORMOSA NINGBO
218
- Unit Price:US$ 2,916 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:High gloss level
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R 级, 23°C | ASTM D785 | 105 |
| R 计秤, 23°C | ISO 2039-2 | 105 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8 MPa, 未退火, 12.7 mm | ASTM D648 | 84.0 °C |
| 1.8 MPa, 退火3 | ASTM D648 | 94.0 °C | |
| vicat | ISO 306/A | 100 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0 kg | ASTM D1238 | 4.0 g/10 min |
| 220°C/10.0 kg | ASTM D1238 | 40 g/10 min |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 70 to 80 °C | ||
| drying time | 2.0 to 3.0 hr | ||
| Processing (melt) temperature | 180 to 230 °C | ||
| mold temperature | 40 to 80 °C | ||
| Injection Pressure | 58.8 to 108 Mpa |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 23°C | ASTM D638 | 43.0 Mpa |
| flexural modulus | 23°C | ASTM D790 | 2450 Mpa |
| bending strength | 23°C | ASTM D790 | 75.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.