ABS

ABS POLYLAC® PA-777D TAIWAN CHIMEI

520

Unit Price:US$ 2,757 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
417MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
ABS D-470 GPPC TAIWAN

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:heat-resisting｜Medium impact resistance
Application Areas:Home appliance components｜Electronic field｜Electrical field｜Automotive sector
Color:--
Grade:Heat resistant grade

Material Certification

MSDS

RoHS

SGS

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179	7.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	14 kJ/m²
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	170 J/m
	Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	140 J/m
		Impact strength of cantilever beam gap	-30°C	ISO 180/1A	7.0 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	13 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield4	ASTM D638	44.0 Mpa
	tensile strength	Yield	ISO 527-2/50	45.0 Mpa
	tensile strength	tensile strength	Break	ISO 527-2/50	33.0 Mpa
elongation	Break4	ASTM D638	15 %
elongation	elongation	Break	ISO 527-2/50	34 %
Bending modulus	--5	ASTM D790	2210 Mpa
Bending modulus	Bending modulus	--6	ISO 178	2300 Mpa
bending strength	--5	ASTM D790	66.5 Mpa
bending strength	bending strength	--6	ISO 178	73.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD	ISO 11359-2	8.5E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	105 °C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	97.0 °C
		Hot deformation temperature	1.8MPa,Annealed	ASTM D648	115 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	117 °C
Vicat softening temperature	--	ASTM D15257	125 °C
	Vicat softening temperature	--	ISO 306/A50	124 °C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	117 °C

Physical properties	Test Condition	Test Method	Test Result
density	--3	ASTM D792	1.06 g/cm³
density	density	23°C	ISO 1183	1.06 g/cm³
melt mass-flow rate	220°C/10.0kg	ASTM D1238	5.5 g/10min
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	5.50 cm3/10min
Shrinkage rate		ISO 294-4	0.30-0.60 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	115

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS POLYLAC® PA-777D TAIWAN CHIMEI

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet