PC LEXAN™ BX7241-7A1D330 SABIC INNOVATIVE NANSHA
142
- Unit Price:US$ 3,620 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:17.8MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Thermal stability｜High gloss
- Application Areas:household electrical appliances｜Casters｜Electrical applications｜Thin walled components
- Color:--
- Grade:--
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | ASTM D648 | 103 °C | |
| ASTM D648 | 93.0 °C | ||
| ball-indentation hardness | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | ASTME831 | 5.9E-05 cm/cm/°C | |
| ASTME831 | 5.9E-05 cm/cm/°C | ||
| RTI Elec | UL 746 | 80.0 °C | |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI | UL 746 | 80.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | IEC 60695-2-13 | 800 °C | |
| IEC 60695-2-13 | 825 °C | ||
| IEC 60695-2-13 | 825 °C | ||
| UL flame retardant rating | UL 94 | V-2 | |
| UL 94 | V-1 | ||
| UL 94 | V-0 | ||
| UL 94 | 5VB | ||
| UL 94 | 5VA |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| --1 | ASTM D638 | 2500 Mpa | |
| yield | ASTM D638 | 67.0 Mpa | |
| ISO 527-2/50 | 62.0 Mpa | ||
| fracture | ASTM D638 | 65.0 Mpa | |
| ISO 527-2/50 | 45.0 Mpa | ||
| yield | ASTM D638 | 4.4 % | |
| ISO 527-2/50 | 4.2 % | ||
| fracture | ASTM D638 | 120 % | |
| ISO 527-2/50 | 90 % | ||
| 50.0mm span | ASTM D790 | 2450 Mpa | |
| --7 | ISO 178 | 2600 Mpa | |
| --8 | ISO 178 | 98.0 Mpa | |
| --9 | ISO 178 | 99.0 Mpa | |
| Yield, 50.0mm span | ASTM D790 | 107 Mpa | |
| Fracture, 50.0mm span | ASTM D790 | 105 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| -30°C | ASTM D256 | 190 J/m | |
| 0°C | ASTM D256 | 420 J/m | |
| 23°C | ASTM D256 | 690 J/m | |
| -30°C | ISO 180/1A | 11 kJ/m² | |
| 0°C | ISO 180/1A | 11 kJ/m² | |
| 23°C | ISO 180/1A | 28 kJ/m² | |
| Dart impact | ASTM D3763 | 60.0 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 18 g/10min | |
| Melt volume flow rate | ISO 1133 | 18.0 cm3/10min | |
| shrinkage rate | 内部方法 | 0.40-0.60 % | |
| Water absorption rate | ISO 62 | 0.20 % | |
| ISO 62 | 0.10 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | >2.0E+15 ohms | |
| volume resistivity | ASTM D257 | >1.0E+16 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| Hot wire ignition (HWI) | UL 746 | PLC 4 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.