'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC/PET XYLEX™ X8300MR-NA9A002 SABIC INNOVATIVE US
18
- Unit Price:US$ 5,200 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :Guangzhou port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Transaction Guarantee:
Supplier Information
Huizhou Rijing Chemical Technology Co., Ltd.
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜High heat resistance
- Application Areas:Automotive Applications｜Electronic and electrical accessories
- Color:--
- Grade:Injection grade
Technical Data Sheet
| optical performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| turbidity | 2540 μm | ASTM D1003 | 1.0 | % |
| transmissivity | 2540 μm | ASTM D1003 | 88.0 | % |
| Refractive index | ISO 489 | 1.539 | ||
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 95.0 | J |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Burning wire flammability index | 1.0 mm | IEC 60695-2-12 | 750 | °C |
| UL flame retardant rating | 3.0 mm | UL 94 | V-2 | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile modulus | --2 | ASTM D638 | 1520 | Mpa |
| -- | ISO 527-2/1 | 1600 | Mpa | |
| tensile strength | Yield3 | ASTM D638 | 47.0 | Mpa |
| Yield | ISO 527-2/50 | 55.0 | Mpa | |
| Break3 | ASTM D638 | 46.0 | Mpa | |
| Break | ISO 527-2/50 | 54.0 | Mpa | |
| elongation | Yield3 | ASTM D638 | 5.0 | % |
| Yield | ISO 527-2/50 | > 5.0 | % | |
| Break3 | ASTM D638 | 150 | % | |
| Break | ISO 527-2/50 | > 200 | % | |
| Bending modulus | 50.0 mm Span4 | ASTM D790 | 1680 | Mpa |
| --5 | ISO 178 | 1700 | Mpa | |
| bending strength | --5,6 | ISO 178 | 78.0 | Mpa |
| Yield, 50.0 mm Span4 | ASTM D790 | 71.0 | Mpa | |
| injection | Test Condition | Test Method | Test Result | Test Unit |
| Exhaust hole depth | 0.013 to 0.020 | mm | ||
| Screw speed | 20 to 100 | rpm | ||
| Back pressure | 0.200 to 0.500 | Mpa | ||
| Mold temperature | 45 to 60 | °C | ||
| Processing (melt) temperature | 245 to 265 | °C | ||
| Spray nozzle temperature | 245 to 265 | °C | ||
| Temperature at the front of the material cylinder | 245 to 265 | °C | ||
| Temperature in the middle of the barrel | 240 to 260 | °C | ||
| Temperature at the rear of the barrel | 240 to 250 | °C | ||
| Suggested injection volume | 40 to 80 | % | ||
| Suggested maximum moisture content | 0.020 | % | ||
| drying time | 3.0 to 5.0 | hr | ||
| drying temperature | 65 to 75 | °C | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 79.0 | °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 75.0 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span9 | ISO 75-2/Ae | 80.0 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8 | ISO 75-2/Af | 78.0 | °C | |
| Vicat softening temperature | -- | ASTM D152510 | 91.0 | °C |
| -- | ISO 306/B120 | 96.0 | °C | |
| Ball Pressure Test | 85°C | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831 | 1.1E-4 | cm/cm/°C |
| Flow : 23 to 60°C | ISO 11359-2 | 9.0E-5 | cm/cm/°C | |
| Across Flow : -40 to 40°C | ASTM E831 | 1.1E-4 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 1.1E-4 | cm/cm/°C | |
| Across Flow : 23 to 60°C | ISO 11359-2 | 9.0E-5 | cm/cm/°C | |
| thermal conductivity | ISO 8302 | 0.23 | W/m/K | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| melt mass-flow rate | 265°C/2.16 kg | ASTM D1238 | 15 | g/10 min |
| Melt Volume Flow Rate (MVR) | 265°C/2.16 kg | ISO 1133 | 15.0 | cm3/10min |
| Shrinkage rate | Flow : 3.20 mm | Internal Method | 0.50 - 0.80 | % |
| Across FlowFlow : 3.20 mm | Internal Method | 0.40 - 0.60 | % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.050 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.20 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Surface resistivity | ASTM D257 | > 1.0E+15 | ohms | |
| Volume resistivity | ASTM D257 | > 1.0E+15 | ohms·cm | |
| Compared to the anti leakage trace index | UL 746 | PLC 0 | ||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Shore hardness | Shore D, 10 Sec | ASTM D2240 | 73 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.