PC IUPILON™ GSH2030R2 MITSUBISHI ENGINEERING JAPAN
315
- Unit Price:US$ 6,874 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜Filler: Glass fiber reinforced material｜30% filler by weight
- Application Areas:Automotive Applications｜electrical equipment
- Color:--
- Grade:Enhanced level
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 148 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 144 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.8E-05 cm/cm/°C |
| TD | ISO 11359-2 | 6.3E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 50 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | MD:3.20mm | 0.050-0.25 % | |
| 吸水率(饱和,23°C) | 0.090 % | ||
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 5.7 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 4.80 cm3/10min |
| shrinkage rate | TD:3.20mm | 0.25-0.45 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 2E+15 ohms | |
| volume resistivity | IEC 60093 | 2E+16 ohms·cm | |
| dielectric strength | 1.00mm | IEC 60243-1 | 32 KV/mm |
| 3.00mm | IEC 60243-1 | 20 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.60 |
| 1MHz | IEC 60250 | 3.50 | |
| Dissipation Factor | 100Hz | IEC 60250 | 1.1E-03 |
| 1MHz | IEC 60250 | 8.4E-03 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 8900 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 120 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.5 % |
| flexural modulus | ISO 178 | 8500 Mpa | |
| bending strength | ISO 178 | 180 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.