Material Description

Material Properties:Low viscosity｜Low flow
Application Areas:Industrial applications｜Automotive sector｜Electronic field｜Electrical field｜currency
Color:--
Grade:--

Technical Data Sheet Compare

hardness	Test Condition	Test Method	Test Result
ball-indentation hardness		ISO 2039-1	116 Mpa

optical performance	Test Condition	Test Method	Test Result
transmissivity		ISO 13468-2	87.0 %
Haze ratio		ISO 14782	<0.80 %
transmissivity		ISO 13468-2	89.0 %
	transmissivity		ISO 13468-2	88.0 %
	transmissivity	transmissivity		ISO 13468-2	89.0 %
refractive index		ISO 489	1.586

thermal performance	Test Condition	Test Method	Test Result
vicat		ISO 306/B120	145 °C
vicat	vicat		ISO 306/B50	143 °C
Heat Deflection Temperature		ISO 75-2/B	136 °C
Heat Deflection Temperature	Heat Deflection Temperature		ISO 75-2/A	123 °C
Glass Transition Temperature		ISO 11357-2	144 °C
RTI Str		UL 746	125 °C
RTI Imp		UL 746	115 °C
RTI Elec		UL 746	125 °C
Linear coefficient of thermal expansion		ISO 11359-2	6.5E-05 cm/cm/°C
thermal conductivity		ISO 8302	0.20 W/m/K
Linear coefficient of thermal expansion		ISO 11359-2	6.5E-05 cm/cm/°C
ball-indentation hardness		IEC 60695-10-2	Pass

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB
UL flame retardant rating	UL flame retardant rating		UL 94	V-2
Burning wire flammability index		IEC 60695-2-12	850 °C
Burning wire flammability index	Burning wire flammability index		IEC 60695-2-12	875 °C
SelfIgnitionTemperature		ASTM D1929	550 °C
needle flame test		IEC 60695-11-5	0.2 min
	needle flame test		IEC 60695-11-5	0.1 min
		needle flame test		IEC 60695-11-5	2.0 min
			needle flame test		IEC 60695-11-5	0.1 min
				needle flame test		IEC 60695-11-5	2.0 min
				needle flame test	needle flame test		IEC 60695-11-5	1.0 min
Burning rate - US-FMVSS		ISO 3795	passed
FlashIgnitionTemperature		ASTM D1929	480 °C
ApplicationofFlamefromSmallBurner-Method		DIN 53438-1,-3	K1.F1
Limiting Oxygen Index		ISO 4589-2	28 %
Hot filament ignition temperature		IEC 60695-2-13	875 °C
	Hot filament ignition temperature		IEC 60695-2-13	875 °C
		Hot filament ignition temperature		IEC 60695-2-13	875 °C
		Hot filament ignition temperature	Hot filament ignition temperature		IEC 60695-2-13	875 °C
Burning wire flammability index		IEC 60695-2-12	930 °C

Supplementary Information	Test Condition	Test Method	Test Result
electrolytic corrosion		IEC 60426	A1

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 7391	12 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 7391	55 kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch		ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap		ISO 7391	12 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 7391	55 kJ/m²
Multi axis Instrumented Peak Impact Force		ISO 6603-2	4900 N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force		ISO 6603-2	5900 N
Multi axis Instrumented Impact Energy		ISO 6603-2	55.0 J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy		ISO 6603-2	60.0 J

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	2400 Mpa
tensile strength		ISO 527-2/50	65.0 Mpa
tensile strength	tensile strength		ISO 527-2/50	60.0 Mpa
Tensile strain		ISO 527-2/50	6.0 %
Tensile strain	Tensile strain		ISO 527-2/50	120 %
Nominal tensile fracture strain		ISO 527-2/50	>50 %
Tensile creep modulus		ISO 899-1	2100 Mpa
Tensile creep modulus	Tensile creep modulus		ISO 899-1	1700 Mpa
bending strength		ISO 178	74.0 Mpa
bending strength	bending strength		ISO 178	98.0 Mpa
Bending Strain		ISO 178	7.0 %
flexural modulus		ISO 178	2350 Mpa

film	Test Condition	Test Method	Test Result
GasPermeation		ISO 2556	150 cm³/m²/bar/24hr
	GasPermeation		ISO 2556	3150 cm³/m²/bar/24hr
		GasPermeation		ISO 2556	750 cm³/m²/bar/24hr
			GasPermeation		ISO 2556	18900 cm³/m²/bar/24hr
			GasPermeation	GasPermeation		ISO 2556	4500 cm³/m²/bar/24hr
Water Vapor Transmission Rate		ISO 15106-1	15 g/m²/24hr
GasPermeation		ISO 2556	630 cm³/m²/bar/24hr

Electrical performance	Test Condition	Test Method	Test Result
Compared to the Leakage Tracking Index (CTI)		IEC 60112	V
Dissipation Factor		IEC 60250	5E-04
Dissipation Factor	Dissipation Factor		IEC 60250	9E-03
relative permittivity		IEC 60250	3.00
relative permittivity	relative permittivity		IEC 60250	3.10
Compared to the Leakage Tracking Index (CTI)		IEC 60112	V
volume resistivity		IEC 60093	1E+16 ohms·cm
dielectric strength		IEC 60243-1	34 KV/mm
Surface Resistivity		IEC 60093	1E+16 ohms

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate		ISO 294-4	0.65 %
shrinkage rate	shrinkage rate		ISO 294-4	0.65 %
Water absorption rate		ISO 62	0.30 %
Water absorption rate	Water absorption rate		ISO 62	0.12 %
Apparent density		ISO 60	0.66 g/cm³
density		ISO 1183	1.19 g/cm³
shrinkage rate		ISO 2577	0.50-0.70 %
shrinkage rate	shrinkage rate		ISO 2577	0.50-0.70 %
Melt volume flow rate		ISO 1133	34.0 cm3/10min
melt mass-flow rate		ISO 1133	37 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.