PPO NORYL GTX™ GTX830-BK1A183N SABIC INNOVATIVE US

Unit Price:US$ 3,900 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Dongguan Lerui Plastic Co., Ltd

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:dimensional stability ｜High temperature resistance
Application Areas:Electrical applications｜Industrial machinery
Color:--
Grade:Injection grade

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5 mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield, 100 mm Span	ASTM D790	248	Mpa
Bending modulus	100 mm Span	ASTM D790	8580	Mpa
elongation	Break	ASTM D638	7.0	%
tensile strength	Break	ASTM D638	158	Mpa
tensile strength	tensile strength	Yield	ASTM D638	151	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying time			3.0 to 4.0	hr
Suggested maximum moisture content			0.070	%
Suggested injection volume			30 to 50	%
Temperature at the rear of the barrel			265 to 305	°C
drying temperature			95 to 105	°C
Temperature in the middle of the barrel			270 to 305	°C
Temperature at the front of the material cylinder			275 to 305	°C
Spray nozzle temperature			280 to 305	°C
Processing (melt) temperature			280 to 305	°C
Mold temperature			75 to 120	°C
Back pressure			0.300 to 1.40	Mpa
Screw speed			20 to 100	rpm
Exhaust hole depth			0.013 to 0.038	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI		UL 746	50.0	°C
RTI Imp		UL 746	50.0	°C
RTI Elec		UL 746	50.0	°C
Linear coefficient of thermal expansion	-20 to 150°C，Flow	ASTM E831	2.0E-5 - 3.1E-5	cm/cm/°C
Vicat softening temperature		ASTM D15255	248	°C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	240	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	254	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 50% RH	ASTM D570	1.0	%
Water absorption rate	Water absorption rate	24 hr, 50% RH	ASTM D570	0.50	%
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.65 - 0.85	%
Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	Internal Method	0.20 - 0.30	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Hot wire ignition		UL 746	PLC 0
High voltage arc tracing rate		UL 746	PLC 1
High arc combustion index		UL 746	PLC 2
Compared to the anti leakage trace index		UL 746	PLC 2
Arc resistance		ASTM D495	PLC 6
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
ASIAPLAS	US$ 3970 /MT
Dongguan Junlong	US$ 5190 /MT

Supplier Join

Get App

Top

PPO NORYL GTX™ GTX830-BK1A183N SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index