PPA AMODEL® AS-4133L-BK324 SOLVAY USA
314
- Unit Price:US$ 6,963 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:52MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Aging resistance｜High temperature resistance｜Filler: Glass fiber reinforced material｜33% filler by weight
- Application Areas:Automotive components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 23℃,24hr | % | 0.30to0.51 | |
| Balance, 23 ℃, 50% RH | % | 0.21to1.2 | |
| Lateral flow: 23 ℃ | mm/mm | 119.4E-3-0.254 | |
| 23℃,24hr | % | 0.12to0.30 | |
| Flow: 23 ℃ | mm/mm | 48.3E-3-129.5E-3 |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | 125 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | % | 23to25 | |
| Burning wire flammability index | °C | 743to960 | |
| Hot filament ignition temperature | °C | 721to926 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Fracture, 23 ℃ | 162.76to199.31 MPa | ||
| Yield, 23 ℃ | % | 1.5to2.6 | |
| 12.62to270.34 MPa | |||
| Fracture, 23 ℃ | 108.28to262.76 MPa | ||
| shear strength | 88.28to107.59 MPa | ||
| Yield, 23 ℃ | 102.76to362.76 MPa | ||
| Poisson's ratio | 0.41 | ||
| compressive strength | 142.76to196.55 MPa | ||
| Yield, 23 ℃ | % | 1.4to2.5 | |
| Fracture, 23 ℃ | % | 1.5to3.1 | |
| % | 1.0to2.5 | ||
| Tensile modulus | 0.15to0.52 | ||
| Yield, 23 ℃ | 68.97to250.34 MPa | ||
| Fracture, 23 ℃ | 131.72to400.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | kJ/m² | 4.178to19.964 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | V | ||
| V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| flow | mm/mm/°C | 195.6E-5-25.4E-5 | |
| vicat | °C | 258to313 | |
| RTI Imp | °C | 118to150 | |
| RTI Elec | °C | 140to150 | |
| flow | mm/mm/°C | 38.1E-5-50.8E-5 | |
| 1.8MPa, Not annealed | °C | 249to304 | |
| flow | mm/mm/°C | 185.4E-5-25.4E-5 | |
| 8.0Mpa, Not annealed | °C | 165to230 | |
| 1.8MPa, Not annealed | °C | 247to292 | |
| 0.45MPa, annealing | °C | 296to320 | |
| 0.45MPa, Not annealed | °C | 275to308 | |
| RTI | °C | 119to150 | |
| Continuous use temperature | °C | 140to186 | |
| horizontal | mm/mm/°C | 68.6E-5-127.0E-5 | |
| 1.8MPa, annealing | °C | 283to300 | |
| horizontal | mm/mm/°C | 63.5E-5-177.8E-5 | |
| 0.45MPa, Not annealed | °C | 273to312 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.