Material Properties:High temperature resistance｜High resistance｜Glass fiber reinforced｜High rigidity｜wear resistant｜Filler: Glass fiber reinforced material｜35% filler by weight
Application Areas:Electrical appliances｜Household appliances｜Automotive interior parts
Color:--
Grade:Flame retardant grade

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
vicat	熔融温度	ISO 11357-3	300 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	2E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	6E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	MD2.0mm	ISO 294-4	0.20 %
shrinkage rate	shrinkage rate	TD2.0mm	ISO 294-4	0.50 %

Electrical performance	Test Condition	Test Method	Test Result
volume resistivity		IEC 60093	>1.0E+15 Ω.cm
dielectric strength	0.250mm	IEC 60243-1	33 KV/mm
Dissipation Factor	相对漏电起痕指数	IEC 60112	575 V

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	23°C	ISO 527-2	185 Mpa
Elongation at break	23°C	ISO 527-2	2.70 %
Tensile modulus	23°C	ISO 527-2	10500 Mpa
Charpy Notched Impact Strength	23°C	ISO 179/1eA	11 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	82 kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.