PC/PET XYLEX™ X7300 7A1D136T SABIC INNOVATIVE NANSHA
202
- Unit Price:US$ 3,780 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:42MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:UV resistance｜High mobility
- Application Areas:Automotive sector
- Color:--
- Grade:Food grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| TD：23to60°C | ISO 11359-2 | 8.5E-05 cm/cm/°C | |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 102 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 88.0 °C | |
| 1.8MPa,Unannealed,100mmSpan | ISO 75-2/Ae | 90.0 °C | |
| vicat | ASTM D15259 | 108 °C | |
| ISO 306/B120 | 106 °C | ||
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 1.2E-04 cm/cm/°C |
| MD：23到60°C | ISO 11359-2 | 8.5E-05 cm/cm/°C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmissivity | 2540µm | ASTM D1003 | 88.0 % |
| Haze ratio | 2540µm | ASTM D1003 | 2.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 9.0 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 95.0 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 265°C/2.16kg | ASTM D1238 | 21 g/10min |
| Melt volume flow rate | 265°C/2.16kg | ISO 1133 | 21.0 cm3/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.80 % |
| TD：3.20mm | 内部方法 | 0.50-0.70 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 1840 Mpa | |
| ISO 527-2/1 | 1900 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 49.0 Mpa |
| 屈服 | ISO 527-2/50 | 55.0 Mpa | |
| 断裂 | ASTM D638 | 52.0 Mpa | |
| 断裂 | ISO 527-2/50 | 55.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 5.0 % |
| Tensile strain | 屈服 | ISO 527-2/50 | 5.0 % |
| elongation | 断裂 | ASTM D638 | 150 % |
| Tensile strain | 断裂 | ISO 527-2/50 | >150 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 1940 Mpa |
| ISO 178 | 2000 Mpa | ||
| bending strength | ISO 178 | 71.0 Mpa | |
| 屈服,50.0mm跨距 | ASTM D790 | 83.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.