Material Description

Material Properties:Low warpage｜Good forming performance｜Glass fiber reinforced
Application Areas:--
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	6.40 mm	ASTM D256	280 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.30 mm	UL 94	V-0
Extreme Oxygen Index		ASTM D2863	46 %

mechanical properties	Test Condition	Test Method	Test Result
tensile strength		ASTM D638	126 Mpa
elongation	Break	ASTM D638	4.3 %
Bending modulus	23°C	ASTM D790	13500 Mpa
bending strength	23°C	ASTM D790	134 Mpa
shear strength		ASTM D732	50.0 Mpa
Poisson's ratio		ASTM E132	0.39

injection	Test Condition	Test Method	Test Result
drying temperature			120 to 150 °C
drying time			3.0 hr
Suggested maximum material return ratio			30 %
Temperature at the rear of the barrel			300 to 320 °C
Temperature in the middle of the barrel			320 to 350 °C
Temperature at the front of the material cylinder			340 to 370 °C
Spray nozzle temperature			340 to 370 °C
Mold temperature			70 to 160 °C
Injection pressure			78.0 to 157 Mpa
Injection speed			中等偏快
Maintain pressure			20.0 to 39.0 Mpa
Back pressure			0.980 to 4.90 Mpa
Screw speed			50 to 100 rpm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	284 °C
Linear coefficient of thermal expansion	Flow : 50 to 150°C	ASTM D696	1.1E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 50 to 150°C	ASTM D696	6.5E-5 cm/cm/°C
RTI Elec	3.2 mm	UL 746	220 °C
RTI Imp	3.2 mm	UL 746	200 °C
RTI	3.2 mm	UL 746	240 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	Flow	ASTM D955	0.22 %
Shrinkage rate	Shrinkage rate	Across FlowFlow	ASTM D955	0.66 %
Water absorption rate	Saturation	ASTM D570	0.020 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ASTM D257	1.0E+15 ohms·cm
Dielectric constant	1 kHz	ASTM D150	4.30
Dielectric constant	Dielectric constant	1 MHz	ASTM D150	3.90
Dissipation factor	1 kHz	ASTM D150	0.019
Dissipation factor	Dissipation factor	1 MHz	ASTM D150	0.028
Arc resistance		ASTM D495	130 sec
Compared to the anti leakage trace index		UL 746	PLC 4

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	103

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.