PBT Cristin® SK645FR NC010 DUPONT USA
203
- Unit Price:US$ 3,579 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:68.8MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Glass fiber reinforced｜Filler: Glass fiber reinforced material｜20% filler by weight
- Application Areas:Electronic and electrical components｜Automotive Applications
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 220 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 210 °C | |
| vicat | ISO 306/B50 | 212 °C | |
| melting temperature | ISO 11357-3 | 225 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 3E-05 cm/cm/°C |
| TD | ISO 11359-2 | 9E-05 cm/cm/°C | |
| Combustibility (rate) | UL 94 | V-0 | |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 200 °C |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 阻燃 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-0 | |
| 0.75mm | IEC 60695-11-10,-20 | V-0 | |
| 1.5mm | IEC 60695-11-10,-20 | V-0 | |
| Limiting Oxygen Index | ISO 4589-2 | 31 % | |
| FMVSS flammability | FMVSS302 | DNI | |
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-0 | |
| 0.75mm | IEC 60695-11-10,-20 | V-0 | |
| 1.5mm | IEC 60695-11-10,-20 | V-0 | |
| Limiting Oxygen Index | ISO 4589-2 | 32 % | |
| FMVSS flammability | FMVSS302 | DNI |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 57 kJ/m² |
| 23°C | ISO 179/1eU | 53 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 40 kJ/m² |
| 23°C | ISO 180/1U | 40 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 50 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1E+15 ohms | |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 39 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 4.50 |
| 1MHz | IEC 60250 | 3.80 | |
| Dissipation Factor | 100Hz | IEC 60250 | 3E-03 |
| 1MHz | IEC 60250 | 0.016 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| IEC 60112 | PLC 3 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | TD2 | ISO 294-4 | 1.5 % |
| TD | ISO 294-4 | 1.2 % | |
| MD | ISO 294-4 | 0.30 % | |
| MD2 | ISO 294-4 | 0.50 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.30 % |
| 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.10 % | |
| MediumDensity | 1.49 g/cm³ | ||
| Ejection Temperature | 170 °C | ||
| SpecificHeatCapacity of Melt | 1600 J/kg/°C | ||
| ThermalConductivityofMelt | 0.26 W/m/K | ||
| density | ASTM D792/ISO 1183 | 1.71 | |
| shrinkage rate | MD | ISO 294-4 | 0.50 % |
| MD2 | ISO 294-4 | 0.60 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.32 % |
| 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.13 % | |
| Ejection Temperature | 170 °C |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile creep modulus | 1000hr | ISO 899-1 | 8000 Mpa |
| bending strength | ISO 178 | 215 Mpa | |
| Tensile modulus | ISO 527-2 | 11200 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 125 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.4 % |
| Tensile creep modulus | 1hr | ISO 899-1 | 11000 Mpa |
| Tensile modulus | ASTM D638/ISO 527 | 11200 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 215 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO 527-2 | 8300 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 110 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.8 % |
| bending strength | ISO 178 | 165 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.