POM LNP™ LUBRICOMP™ KL-4030 SABIC INNOVATIVE US

307

Unit Price:US$ 5,570 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
75MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low extract｜wear resistant
Application Areas:Plastic bag｜Medical and nursing supplies
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	46	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	3.0	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Wear factor	Washer	ASTM D3702Modified	11.0	10^-10in^5-min/ft-lb-hr
Wear factor	Wear factor	Ring	ASTM D3702Modified	0.300	10^-10in^5-min/ft-lb-hr
Friction coefficient	Static	ASTM D3702Modified	0.17
Friction coefficient	Friction coefficient	Dynamic	ASTM D3702Modified	0.35
bending strength		ASTM D790	75.8	Mpa
Bending modulus		ISO 178	2250	Mpa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	2210	Mpa
Tensile strain	Break	ISO 527-2/5	16	%
elongation	Break	ASTM D638	19	%
Tensile strain	Yield	ISO 527-2/5	9.0	%
elongation	Yield	ASTM D638	10	%
tensile strength	Break	ISO 527-2/5	46.0	Mpa
	tensile strength	Break	ASTM D638	48.0	Mpa
		tensile strength	Yield	ISO 527-2/5	46.0	Mpa
		tensile strength	tensile strength	Yield	ASTM D638	48.0	Mpa
Tensile modulus		ISO 527-2/1	2460	Mpa
Tensile modulus	Tensile modulus		ASTM D638	2530	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	149	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	97.0	°C
		Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	158	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	88.0	°C
Linear coefficient of thermal expansion	MD：-30to30°C	ASTM D696	1.1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-30to30°C	ASTM D696	1.1E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	24hr,50%RH	ASTM D570	0.20	%
Shrinkage rate	TD：24hr	ASTM D955	1.0-3.0	%
Shrinkage rate	Shrinkage rate	MD：24hr	ASTM D955	1.0-3.0	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.29	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

POM LNP™ LUBRICOMP™ KL-4030 SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index