Material Description

Material Properties:High mobility｜High ductility at low temperature｜Short molding cycle
Application Areas:Lighting applications｜Electronic and Electrical Applications｜Aerospace Applications｜Plastic bag
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Dart impact	23°C, Total Energy	ASTM D3763	67.0 J
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	70 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	35 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA
Burning wire flammability index	1.5 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.5 mm	IEC 60695-2-13	825 °C
Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	825 °C

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield, 50.0 mm Span4	ASTM D790	92.0 Mpa
bending strength	bending strength	--5,6	ISO 178	87.0 Mpa
Bending modulus	--5	ISO 178	2100 Mpa
Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	2400 Mpa
elongation	Break	ISO 527-2/50	110 %
	elongation	Break3	ASTM D638	120 %
		elongation	Yield	ISO 527-2/50	6.0 %
		elongation	elongation	Yield3	ASTM D638	6.0 %
tensile strength	Break	ISO 527-2/50	57.0 Mpa
	tensile strength	Break3	ASTM D638	59.0 Mpa
		tensile strength	Yield	ISO 527-2/50	56.0 Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	58.0 Mpa
Tensile modulus	--	ISO 527-2/1	2000 Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2100 Mpa

injection	Test Condition	Test Method	Test Result
Exhaust hole depth			0.025 to 0.076 mm
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
drying temperature			120 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 60 %
Temperature at the rear of the barrel			270 to 295 °C
Temperature in the middle of the barrel			280 to 305 °C
Temperature at the front of the material cylinder			295 to 315 °C
Spray nozzle temperature			290 to 310 °C
Processing (melt) temperature			295 to 315 °C
Mold temperature			70 to 95 °C

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	123 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	118 °C
Vicat softening temperature	--	ASTM D152510	140 °C
	Vicat softening temperature	--	ISO 306/B50	139 °C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	141 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.1E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	6.2E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	6.2E-5 cm/cm/°C
RTI Elec		UL 746	125 °C
RTI Imp		UL 746	115 °C
RTI		UL 746	120 °C

Physical properties	Test Condition	Test Method	Test Result
Outdoor applicability		UL 746C	f1
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.15 %
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.40 %
Shrinkage rate	3.20 mm，Flow	Internal Method	0.40 - 0.80 %
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	15.0 cm3/10min
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	16 g/10 min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.