PPS PPS-hGR50 SICHUAN DEYANG
193
- Unit Price:US$ 4,491 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:14MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High temperature resistance
- Application Areas:Aerospace｜Automotive sector｜Electrical appliances｜Electronic field｜Electrical field
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | GB/T 15585-1995 | 0.0025 mm/mm |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | GB/T 1033-1986 | 1.68 g/cm³ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation at break | ASTM D638/ISO 527 | 1.9 % | |
| tensile strength | ASTM D638/ISO 527 | 176 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 111 | |
| bending strength | ASTM D790/ISO 178 | 285 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | 1.63*100000 % | |
| Flexural modulus | GB/T 1042-1992 | 1.63×104 Mpa | |
| bending strength | GB/T 1042-1992 | 284.7 Mpa | |
| Rockwell hardness | GB/T 9342-1988 | 111 hr | |
| elongation | GB/T 1040-1992 | 1.90 % | |
| Impact strength of cantilever beam gap | GB/T 1843-1996 | 13 kJ/m² | |
| compressive strength | GB/T 1041-1992 | 135 Mpa | |
| tensile strength | GB/T 1040-1992 | 176 Mpa |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.68 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | GB/T 1410-1989 | 2.2×1015 Ω | |
| dielectric strength | GB/T 1408.1-1999 | 19.1 KV/mm | |
| dielectric constant | GB/T 1409-1988 | 4 | |
| Volume resistivity | GB/T 1410-1989 | 3.4×1014 Ω.m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | 282 ℃（℉） | ||
| combustibility | GB/T 2408-1996 | FV-0 级 | |
| melting temperature | GB/T 4608-1984 | 282 °C | |
| Heat distortion temperature | GB/T 1634-1979(1989) | 267 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.