Material Properties:Flame retardant｜Thermal stability｜High temperature resistance｜Glass fiber reinforced
Application Areas:Food containers
Color:--
Grade:Injection grade

Technical Data Sheet Compare

Thermal Properties	Test Condition	Test Method	Test Result
RTI Imp		UL 746B	65 °C
	RTI Imp		UL 746B	65 °C
	RTI Imp	RTI Imp		UL 746B	65 °C
RTI Elec		UL 746B	65 °C
	RTI Elec		UL 746B	65 °C
	RTI Elec	RTI Elec		UL 746B	65 °C
Linear coefficient of thermal expansion	流动	ISO 11359-1/-2	14 E-6/K
	Linear coefficient of thermal expansion	-40-23°C，流动	ISO 11359-1/-2	17 E-6/K
		Linear coefficient of thermal expansion	横向	ISO 11359-1/-2	55 E-6/K
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	-40-23°C，横向	ISO 11359-1/-2	55 E-6/K
melting temperature		ISO 11357-1/-3	260 °C

combustibility	Test Condition	Test Method	Test Result
UL flame retardant rating	HB	UL 94	0.75 mm
UL flame retardant rating	UL flame retardant rating	HB	UL 94	1.5 mm
Limiting Oxygen Index (LOI)		ISO 4589-1/-2	27 %
FMVSS combustion rate		FMVSS 302	B -
burning rate	1mm	ISO 3795	25 mm/min

Electrical Property	Test Condition	Test Method	Test Result
volume resistivity		IEC 60093	10000000000000 Ohm-m
Compared to the Leakage Traceability Index (CTI)		IEC 60112	600 -

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	Dry	ISO 179/1eA	15 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Dry，23℃	ISO 179/1eA	95 kJ/m²
Impact strength of cantilever beam gap	Dry，-40℃	ISO 180/1A	15 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Dry，23℃	ISO 180/1A	236 °C

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	Dry，Flow	ISO 294-4	0.2 %
shrinkage rate	shrinkage rate	Dry	ISO 294-4	0.4 %

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Conditione，断裂	ISO 527-1/-2	215 Mpa
tensile strength	tensile strength	Dry，断裂	ISO 527-1/-2	250 Mpa
Elongation at break	Conditio	ISO 527-1/-2	3.2 %
Elongation at break	Elongation at break	Dry	ISO 527-1/-2	2.8 %
flexural modulus	Dry	ISO 178	15000 Mpa
Tensile modulus	Conditio	ISO 527-1/-2	16300 Mpa
Tensile modulus	Tensile modulus	Dry	ISO 527-1/-2	16500 Mpa
Poisson's ratio	Dry	ISO 527-1/-2	14

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.