PC LEXAN™ ML9330 BK1E519 SABIC INNOVATIVE US

Unit Price:US$ 4,620 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Huizhou Rijing Chemical Technology Co., Ltd.

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜Toughening｜UV resistance
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	60	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	75	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	23°C11	Internal Method	1100	J/m
	Suspended wall beam without notch impact strength	-30°C9	ISO 180/1U	无断裂
	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C9	ISO 180/1U	无断裂
Dart impact	23°C,TotalEnergy	ASTM D3763	52.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8mm	UL 94	V-1
	UL flame retardant rating	1.5mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	5VA
Burning wire flammability index	1.0mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	825	°C
Extreme Oxygen Index		ISO 4589-2	35	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
elongation	Break	ISO 527-2/50	130	%
Bending modulus	50.0mmSpan5	ASTM D790	2070	Mpa
Bending modulus	Bending modulus	--6	ISO 178	2200	Mpa
bending strength	--6,7	ISO 178	85.0	Mpa
bending strength	bending strength	Yield,50.0mmSpan5	ASTM D790	88.0	Mpa
Tensile modulus	--3	ASTM D638	2100	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2100	Mpa
tensile strength	Yield4	ASTM D638	58.0	Mpa
	tensile strength	Yield	ISO 527-2/50	55.0	Mpa
		tensile strength	Break4	ASTM D638	61.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	60.0	Mpa
elongation	Yield4	ASTM D638	6.0	%
	elongation	Yield	ISO 527-2/50	6.0	%
	elongation	elongation	Break4	ASTM D638	130	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD:23to80°C	ISO 11359-2	7.2E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,100mmSpan12	ISO 75-2/Ae	124	°C
Vicat softening temperature	--	ASTMD152513	142	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	140	°C
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	124	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	120	°C
		Hot deformation temperature	0.45MPa,Unannealed,100mmSpan12	ISO 75-2/Be	135	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	134	°C
RTI		UL 746	120	°C
RTI Imp		UL 746	115	°C
RTI Elec		UL 746	125	°C
Linear coefficient of thermal expansion	TD:23to80°C	ISO 11359-2	7.7E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	6.7E-05	cm/cm/°C
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	6.7E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	300°C/1.2kg	ASTM D1238	10	g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	9.00	cm3/10min
Shrinkage rate	MD:3.20mm	Internal Method	0.40-0.80	%
Shrinkage rate	Shrinkage rate	TD:3.20mm	Internal Method	0.40-0.80	%
Water absorption rate	Saturation,23°C	ISO 62	0.35	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15	%
Outdoor applicability		UL 746C	f1
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Hot wire ignition	HWI	UL 746	PLC 1
High arc combustion index	HAI	UL 746	PLC 0
Compared to the anti leakage trace index		IEC 60112	PLC 3
Compared to the anti leakage trace index	Compared to the anti leakage trace index	CTI	UL 746	PLC 3
Dissipation factor	60Hz	IEC 60250	1E-03
	Dissipation factor	50Hz	IEC 60250	1E-03
		Dissipation factor	1MHz	ASTMD150	8.5E-03
			Dissipation factor	60Hz	ASTM D150	2.4E-03
			Dissipation factor	Dissipation factor	50Hz	ASTM D150	2.4E-03
Dielectric strength	3.20mm,in Oil	IEC 60243-1	16	KV/mm
Dielectric strength	Dielectric strength	3.20mm,inOil	ASTM D149	17	KV/mm
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Surface resistivity		IEC 60093	>1.0E+15	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	H358/30	ISO 2039-1	90.0	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan Xinmingyuan	US$ 4230 /MT
Dongguan Zhengxingyuan	US$ 4300 /MT
ASIAPLAS	US$ 4500 /MT
Dongguan Senlin	US$ 5850 /MT

Supplier Join

Get App

Top

PC LEXAN™ ML9330 BK1E519 SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index