Basic Performance	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D-792	0.91
melt mass-flow rate	230℃，2.16Kg	ASTM D-1238	0.4	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23℃	ASTM D-256	无破损	kg.cm/cm
Bending modulus		ASTM D-790	11500	kg/cm
Impact strength of cantilever beam gap	-20℃	ASTM D-256	6	kg.cm/cm
Elongation at Break		ASTM D-638	500	%
tensile strength	Yield点	ASTM D-638	270	kg/cm
tensile strength	tensile strength	断点	ASTM D-638	240	kg/cm
Impact strength of cantilever beam gap	0℃	ASTM D-256	10	kg.cm/cm
Charpy Notched Impact Strength		ASTM D256/ISO 179	12	kg·cm/cm(J/M)ft·lb/in
Rockwell hardness		ASTM D785	90
Elongation at Break		ASTM D638/ISO 527	200	kg/cm²(MPa)[Lb/in²]
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	0℃-110℃	Dilatometor	1.5×10	K
Vicat softening temperature		ASTM D-1525	150	°C
Melting temperature		HS Method	162	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		ASTM D1238/ISO 1133	0.4	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		HS Method	>10	Ω

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.