thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	1.8MPa,未退火,6.40mm	ASTM D648	205 °C
melting temperature		ASTM D3418	223 °C
RTI Elec		UL 746	75.0 °C
RTI Imp		UL 746	75.0 °C
RTI Str		UL 746	75.0 °C
Heat Deflection Temperature	0.45MPa,未退火,6.40mm	ASTM D648	215 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	265°C/2.16kg	ASTM D1238	27 g/10min
shrinkage rate	MD	ASTM D955	0.40-1.0 %
Water absorption rate	23°C,24hr	ASTM D570	0.060 %

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break,3.20mm	ASTM D638	118 Mpa
elongation	断裂,3.20mm	ASTM D638	4.0 %
flexural modulus	3.20mm	ASTM D790	8830 Mpa
bending strength	屈服,3.20mm	ASTM D790	186 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.