ABS POLYLAC® PA-765B TAIWAN CHIMEI

279

Unit Price:$3438 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
40.1MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
ABS AF-312C LG CHEM KOREA

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Material Certification

Technical Data Sheet

Material Description

Material Properties:Flame retardant｜Medium impact resistance
Application Areas:Home appliance components｜Fitness equipment｜Electronic field｜Electrical field
Color:--
Grade:Flame retardant grade

Material Certification

Technical Data Sheet Compare

Physical	Test Condition	Test Method	Test Result
Density / Specific Gravity	--3	ASTMD792	1.16 g/cm³
Density / Specific Gravity	Density / Specific Gravity	23°C	ISO1183	1.16 g/cm³
Melt Mass-Flow Rate	200°C/5.0kg	ASTMD1238	4.2 g/10min
Melt Volume flow Rate	220°C/10.0kg	ISO1133	38.0 cm3/10min
Modeling Shrinkage		ISO294-4	0.30到0.60 %

Thermal Properties	Test Condition	Test Method	Test Result
Heat Deflection Temperature	1.8MPa,未退火	ASTMD648	76.0 °C
	Heat Deflection Temperature	1.8MPa,未退火	ISO75-2/A	77.0 °C
	Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,退火	ASTMD648,ISO75-2/A	85.0 °C
Vicat Softening Temperature	--	ASTMD15257	92.0 °C
	Vicat Softening Temperature	--	ISO306/A50	94.0 °C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B50	80.0 °C
Linear thermal expansion coefficient	MD	ISO11359-2	8.6E-05 cm/cm/°C

Flammability	Test Condition	Test Method	Test Result
Flame Rating	1.5mm	UL94	V-2
	Flame Rating	2.5mm	UL94	V-0
	Flame Rating	Flame Rating	3.0mm	UL94	5VA

Mechanical Properties	Test Condition	Test Method	Test Result
Tensile Strength	屈服4	ASTMD638	39.1 Mpa
	Tensile Strength	屈服	ISO527-2/50	38.0 Mpa
	Tensile Strength	Tensile Strength	断裂	ISO527-2/50	29.0 Mpa
Tensile Elongation	断裂4	ASTMD638	25 %
Tensile Elongation	Tensile Elongation	断裂	ISO527-2/50	10 %
Flexural Modulus	--5	ASTMD790	2340 Mpa
Flexural Modulus	Flexural Modulus	--6	ISO178	1800 Mpa
Flexural Strength	--5	ASTMD790	63.4 Mpa
Flexural Strength	Flexural Strength	--6	ISO178	57.0 Mpa

Hardness	Test Condition	Test Method	Test Result
Rockwell Hardness	R级	ASTMD785	102

Impact Properties	Test Condition	Test Method	Test Result
Notched Izod Impact Strength	23°C,3.20mm	ASTMD256	250 J/m
	Notched Izod Impact Strength	23°C,6.40mm	ASTMD256	210 J/m
		Notched Izod Impact Strength	-30°C	ISO180/1A	11 kJ/m²
		Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	24 kJ/m²
Charpy Notched Impact Strength	-30°C	ISO179	11 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179	26 kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.