PBT VALOX™ 310SEO-1001 SABIC INNOVATIVE JAPAN
210
- Unit Price:$7132 USD/MT
- Packaging Specification:25 KG/PKG
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading:China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Material Certification
Technical Data Sheet
Material Description
- Material Properties:Flame retardant
- Application Areas:Industrial applications｜Electrical field｜Electronic field｜Switch panel｜Shell｜currency
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific Volume | ASTMD792 | 0.770 cm³/g | |
| Modeling Shrinkage | MD：--2 | 内部方法 | 0.90to1.6 % |
| MD：--3 | 内部方法 | 1.5to2.3 % | |
| TD：--2 | 内部方法 | 1.0to1.7 % | |
| TD：--3 | 内部方法 | 1.6to2.4 % | |
| Moisture Absorption | 24hr | ASTMD570 | 0.080 % |
| Melt Viscosity | 内部方法 | 600 Pa·s | |
| Specific Volume | ASTM D792 | 0.710 cm³/g | |
| Melt Mass-Flow Rate | 250°C/2.16 kg | ASTM D1238 | 8.6 g/10 min |
| Melt Volume flow Rate | 250°C/2.16 kg | ISO 1133 | 8.00 cm3/10min |
| Modeling Shrinkage | 流动 2 | 内部方法 | 1.1 到 1.8 % |
| 流动 : 0.750 到 2.30 mm | 内部方法 | 0.90 到 1.6 % | |
| 流动 : 3.20 mm | 内部方法 | 1.5 到 2.3 % | |
| 流动 : 2.30 到 4.60 mm | 内部方法 | 1.5 到 2.3 % | |
| 横向流动 2 | 内部方法 | 0.90 到 1.9 % | |
| 横向流动 : 0.750 到 2.30 mm | 内部方法 | 1.0 到 1.7 % | |
| 横向流动 : 2.30 到 4.60 mm | 内部方法 | 1.6 到 2.4 % | |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.36 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.080 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 154 °C |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 54.4 °C | |
| Linear thermal expansion coefficient | MD：-40to40°C | ASTME831 | 8.1E-05 cm/cm/°C |
| MD：60to138°C | ASTME831 | 1.4E-04 cm/cm/°C | |
| RTIElec | UL746 | 120 °C | |
| Evolution Calendar intelligent importer | UL746 | 120 °C | |
| RTIStr | UL746 | 140 °C | |
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 162 °C |
| 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 10 | ISO 75-2/Be | 150 °C | |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 74.0 °C | |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 71.0 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 10 | ISO 75-2/Ae | 60.0 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9 | ISO 75-2/Af | 73.0 °C | |
| Vicat Softening Temperature | -- | ASTM D152511, ISO 306/B50, ISO 306/B120 | 170 °C |
| -- | ISO 306/A50 | 212 °C | |
| Ball PressureTest | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831 | 7.9E-5 cm/cm/°C |
| 流动 : 60 到 138°C | ASTM E831 | 1.3E-4 cm/cm/°C | |
| 流动 : -40 到 40°C | ISO 11359-2 | 7.6E-5 cm/cm/°C | |
| 流动 : 23 到 60°C | ISO 11359-2 | 1.0E-4 cm/cm/°C | |
| 横向 : -40 到 40°C | ASTM E831 | 7.9E-5 cm/cm/°C | |
| 横向 : -40°C | ISO 11359-2 | 7.3E-5 cm/cm/°C | |
| 横向 : 23 到 60°C | ISO 11359-2 | 1.0E-4 cm/cm/°C | |
| Thermal Conductivity | ISO 8302 | 0.24 W/m/K | |
| RTI Elec | UL 746 | 120 °C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI | UL 746 | 140 °C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flame Rating | 1.5mm | UL94 | HB |
| UL flame retardant rating | 0.71 mm | UL 94 | V-0 |
| 3.0 mm | UL 94 | 5VA | |
| Glow Wire Flammability Index | 1.0 mm | IEC 60695-2-12 | 960 °C |
| Oxygen Index | ISO 4589-2 | 30 % |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Strength | 屈服 | ASTMD638 | 51.7 Mpa |
| Break | ASTMD638 | 51.7 Mpa | |
| Tensile Elongation | 断裂 | ASTMD638 | 300 % |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 2340 Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 82.7 Mpa |
| Break,50.0mmSpan | ASTMD790 | 82.7 Mpa | |
| Tensile Modulus | -- 3 | ASTM D638 | 2820 Mpa |
| -- | ISO 527-2/1 | 2800 Mpa | |
| Tensile Strength | 屈服 4 | ASTM D638 | 58.0 Mpa |
| 屈服 | ISO 527-2/50 | 58.0 Mpa | |
| 断裂 4 | ASTM D638 | 52.0 Mpa | |
| 断裂 | ISO 527-2/50 | 40.0 Mpa | |
| Tensile Elongation | 屈服 4 | ASTM D638 | 5.0 % |
| 屈服 | ISO 527-2/50 | 5.0 % | |
| 断裂 4 | ASTM D638 | 18 % | |
| 断裂 | ISO 527-2/50 | 18 % | |
| Flexural Modulus | 50.0 mm 跨距 5 | ASTM D790 | 2620 Mpa |
| -- 6 | ISO 178 | 2600 Mpa | |
| Flexural Stress | -- 6, 7 | ISO 178 | 90.0 Mpa |
| 屈服, 50.0 mm 跨距 5 | ASTM D790 | 101 Mpa | |
| Taber Abrasion Resistance | 1000 Cycles, 1000 g, CS-17 转轮 | 内部方法 | 19.0 mg |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dielectric Constant | 100Hz | ASTMD150 | 3.30 |
| 1MHz | ASTMD150 | 3.10 | |
| Dissipation Factor? | 100Hz | ASTMD150 | 2E-03 |
| 1MHz | ASTMD150 | 0.020 | |
| Arc Resistance | ASTMD495 | PLC 5 | |
| Comparative Tracking Index | CTI | UL746 | PLC 0 |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC 1 |
| Volume Resistivity | ASTMD257 | >4.0E+16 ohms·cm | |
| Dielectric Strength | 1.60mm,inAir | ASTMD149 | 23 KV/mm |
| 1.60mm,在油中 | ASTMD149 | 23 KV/mm | |
| 3.20mm,inAir | ASTMD149 | 16 KV/mm | |
| 3.20mm,在油中 | ASTMD149 | 16 KV/mm | |
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| Volume Resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| Dielectric Strength | 1.60 mm, in Oil | ASTM D149 | 24 KV/mm |
| 3.20 mm, in Air | ASTM D149 | 18 KV/mm | |
| 0.800 mm, 在油中 | IEC 60243-1 | 35 KV/mm | |
| 1.00 mm 12 | IEC 60243-1 | 18 KV/mm | |
| 1.60 mm, 在油中 | IEC 60243-1 | 25 KV/mm | |
| 3.20 mm, 在油中 | IEC 60243-1 | 17 KV/mm | |
| Relative Permittivity | 50 Hz | IEC 60250 | 2.90 |
| 60 Hz | IEC 60250 | 2.90 | |
| 100 Hz | IEC 60250 | 3.10 | |
| 1 MHz | IEC 60250 | 2.80 | |
| Dissipation Factor? | 50 Hz | IEC 60250 | 1.0E-3 |
| 60 Hz | IEC 60250 | 1.0E-3 | |
| 100 Hz | IEC 60250 | 2.0E-3 | |
| 1 MHz | IEC 60250 | 0.013 | |
| Arc Resistance | ASTM D495 | PLC 6 | |
| Comparative Tracking Index | UL 746 | PLC 3 | |
| -- | IEC 60112 | 175 V | |
| 解决方案 B | IEC 60112 | 100 V | |
| High Amp Arc Ignition | UL 746 | PLC 0 | |
| High Voltage Arc Tracking Rate | UL 746 | PLC 6 | |
| UL 746 | PLC 4 | ||
| Hot-wire Ignition | UL 746 | PLC 2 |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature | 120 °C | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Suggested Max Moisture | 0.020 % | ||
| Suggested Shot Size | 40 到 80 % | ||
| Rear Temperature | 230 到 250 °C | ||
| Middle Temperature | 240 到 255 °C | ||
| Front Temperature | 245 到 260 °C | ||
| Nozzle Temperature | 240 到 255 °C | ||
| Processing (Melt) Temp | 245 到 260 °C | ||
| Mold Temperature | 50 到 75 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 50 到 100 rpm | ||
| Vent Depth | 0.013 到 0.025 mm |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell Hardness | R级 | ASTMD785 | 117 |
| R 计秤 | ISO 2039-2 | 120 | |
| Ball Indentation Hardness | H 358/30 | ISO 2039-1 | 105 Mpa |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Gardner Impact | 23°C | ASTMD3029 | 40.7 J |
| 23°C6 | ASTMD3029 | 40.7 J | |
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 | |
| Unnotched Izod Impact Strength | 23°C | ASTM D4812, ISO 180/1U | 无断裂 |
| -30°C 9 | ISO 180/1U | 无断裂 | |
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 200 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.