PPS DURAFIDE® 6165A6 HD9100 JAPAN POLYPLASTIC
272
Unit Price:$8241 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Flame retardant standard High temperature resistan Filler: Glass mineral 65% filler by weight 65% filler by weight
- Application Areas:Fiber grade Pump parts Shell Electrical/Electronic App
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTMD792 | 2.00 | g/cm³ | |
| Specific volume | ASTMD792 | 0.502 | cm³/g | |
| density | ISO1183 | 1.95 | g/cm³ | |
| Shrinkage rate | MD | ASTMD955 | 0.10to0.20 | % |
| TD | ASTMD955 | 0.30to0.50 | % | |
| TD | ISO294-4 | 0.30to0.70 | % | |
| MD | ISO294-4 | 0.20to0.60 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.020 | % |
| 23℃ | ISO 62 | 0.02 | % | |
| density | ISO 1183 | 1.95 | g/cm³ | |
| Shrinkage rate | ISO 2577 | 0.2-0.6 | % | |
| SpecificHeatCapacity of Melt | 内部方法 | 1600 | J/kg/°C |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 100 | M-scale | |
| Tensile modulus | ISO 527-1 | 19000 | Mpa | |
| tensile strength | ISO 527-1 | 130 | Mpa | |
| elongation | Break | ISO 527-1 | 1.2 | % |
| Bending modulus | ISO 178 | 18800 | Mpa | |
| bending strength | ISO 178 | 210 | Mpa | |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 6 | kJ/m² |
| Tensile modulus | ISO527-2/1A/1 | 19000 | Mpa | |
| tensile strength | Break,23°C | ASTMD638 | 114 | Mpa |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 6.0 | kJ/m² |
| Cantilever beam without notch impact strength | 23°C | ISO180/1U | 20 | kJ/m² |
| Rockwell hardness | M-Scale | ASTMD785 | 100 | |
| M-Scale | ISO2039-2 | 100 | ||
| tensile strength | Break | ISO527-2/1A/5 | 130 | Mpa |
| elongation | Break,23°C | ASTMD638 | 1.3 | % |
| Break | ISO527-2/1A/5 | 1.2 | % | |
| Bending modulus | 23°C | ISO178 | 18800 | Mpa |
| bending strength | ISO178 | 210 | Mpa | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 7.0 | kJ/m² |
| 23°C | ISO179/1eA | 7.0 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 20 | kJ/m² |
| 23°C | ISO179/1eU | 20 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 6.0 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.9E-05 | cm/cm/°C |
| TD | ISO11359-2 | 2.4E-05 | cm/cm/°C | |
| Hot deformation temperature | 0.45MPa,Annealed | ASTMD648 | 280 | °C |
| 1.8MPa,Unannealed | ASTMD648 | 266 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 270 | °C | |
| 8.0MPa,Unannealed | ISO75-2/C | 215 | °C | |
| Glass transition temperature | ISO11357-2 | 90.0 | °C | |
| Melting temperature | ISO11357-3 | 280 | °C | |
| Hot deformation temperature | 1.80Mpa | ISO 75-1 | 270 | °C |
| Flame retardant grade | 0.750mm | UL94 | V-0 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | ASTMD257 | 1E+16 | ohms·cm | |
| IEC60093 | >1.0E+15 | ohms·cm | ||
| Dielectric strength | IEC60243-1 | 25 | KV/mm | |
| Dielectric constant | 1kHz | ASTMD150 | 4.50 | |
| 1MHz | ASTMD150 | 4.50 | ||
| Relative permittivity | 1MHz | IEC60250 | 5.60 | |
| Dissipation factor | 1kHz | ASTMD150 | 1E-03 | |
| 1MHz | ASTMD150 | 9E-04 | ||
| 1MHz | IEC60250 | 2E-03 | ||
| Arc resistance | ASTMD495 | 182 | sec | |
| Leakage Trace Index | IEC60112 | 175 | V |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | V-0 | |
| 1.5mm | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.