PPS RYTON® R-4-200BL CPCHEM USA
293
Unit Price:$9477 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 64MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Glass fiber reinforced high strength High temperature resistan Filler: Glass fiber reinf 40% filler by weight
- Application Areas:Bottle cap household electrical appl Casters Electrical applications Automotive Applications Fitness equipment Application in the automo
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTMD792 | 1.68 | g/cm³ | |
| Shrinkage rate | MD：3.20mm | 0.20 | % | |
| TD：3.20mm | 0.50 | % | ||
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.020 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | ASTMD638 | 179 | Mpa | |
| ISO527-2 | 185 | Mpa | ||
| elongation | Break | ASTMD638 | 1.5 | % |
| Break | ISO527-2 | 1.5 | % | |
| Bending modulus | ASTMD790 | 14500 | Mpa | |
| ISO178 | 14000 | Mpa | ||
| bending strength | ASTMD790 | 255 | Mpa | |
| ISO178 | 260 | Mpa | ||
| compressive strength | ASTMD695 | 275 | Mpa | |
| Poisson's ratio | ISO527 | 0.40 | ||
| Impact strength of cantilever beam gap | 3.17mm | ASTMD256 | 80 | J/m |
| ISO180/A | 8.0 | kJ/m² | ||
| Cantilever beam without notch impact strength | 3.18mm | ASTMD4812 | 530 | J/m |
| ISO180 | 35 | kJ/m² | ||
| Rockwell hardness | M-Sale | ASTMD785 | 100 | |
| R-Sale | ASTMD785 | 120 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ASTMD648 | 265 | °C |
| Linear coefficient of thermal expansion | MD：-50to50°C | ASTME831 | 1.5E-05 | cm/cm/°C |
| MD：100to200°C | ASTME831 | 1E-05 | cm/cm/°C | |
| TD：-50to50°C | ASTME831 | 4E-05 | cm/cm/°C | |
| TD：100to200°C | ASTME831 | 8.5E-05 | cm/cm/°C | |
| TD：导热系数 | ASTME831 | 0.33 | W/m/K | |
| UL temperature rating | UL746B | 200to220 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTMD257 | 1E+16 | ohms | |
| Volume resistivity | ASTMD257 | 1E+16 | ohms·cm | |
| Dielectric strength | ASTMD149 | 22 | KV/mm | |
| Dielectric constant | 25°C,1kHz | ASTMD150 | 3.90 | |
| 25°C,1MHz | ASTMD150 | 3.80 | ||
| Dissipation factor | 25°C,1kHz | ASTMD150 | 2E-03 | |
| 25°C,1MHz | ASTMD150 | 2E-03 | ||
| Arc resistance | ASTMD495 | 125 | sec | |
| Compared to the anti leakage trace index | CTI | UL746 | 150 | V |
| InsulationResistance | 90°C | 1E+11 | ohms |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 1.6mm | UL94 | V-05VA | |
| Extreme Oxygen Index | ASTMD2863 | 57 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.