PC/ABS LUPOY® HR5007A-NP LG GUANGZHOU
253
Unit Price:$3042 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 68.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance High mobility High temperature resistan
- Application Areas:Automotive sector Electronic field Electrical field Automotive interior parts Electrical components
- Color:--
- Grade:High liquidity level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 250°C/2.16kg | ASTMD1238 | 5.3 | g/10min |
| Melt Volume-Flow Rate (MVR) | 260°C/5.0kg | ASTMD1505 | 18.0 | cm3/10min |
| Shrinkage rate | MD：3.20mm,InjectionMolded | ASTMD955 | 0.50to0.80 | % |
| Water absorption rate | Saturation | ISO622 | 0.15 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-22 | 2200 | Mpa | |
| tensile strength | Yield,3.20mm,Injection | ASTMD638 | 56.9 | Mpa |
| Yield | ISO527-22 | 60.0 | Mpa | |
| elongation | Yield | ISO527-22 | 4.9 | % |
| Tensile strain | Break,3.20mm,InjectionMolded | ASTMD638 | >100 | % |
| Nominal strainatbreak | ISO527-22 | >50 | % | |
| Bending modulus | 3.20mm,InjectionMolded | ASTMD790 | 2110 | Mpa |
| bending strength | 3.20mm | ASTMD790 | 77.5 | Mpa |
| Charpynotchedimimpact string | 23°C | ISO179/1eA2 | NoBreak | |
| Charpy impact strength | 23°C | ISO179/1eU2 | NoBreak | |
| Charpyimpactstrength | -30°C | ISO179/1eU2 | NoBreak | |
| Rockwell hardness | R-Scale | ASTMD785 | 114 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,6.40mm,InjectionMolded | ASTMD648 | 113 | °C |
| 1.8MPa | ISO75-22 | 104 | °C | |
| Glass transition temperature | ISO11357-22 | 150 | °C | |
| vicat softening point | 50N | ISO3062 | 119 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-22 | 7.7E-05 | cm/cm/°C |
| TD | ISO11359-22 | 8.3E-05 | cm/cm/°C | |
| RTIElec | 1.6mm | UL746 | 60.0 | °C |
| 3.0mm | UL746 | 60.0 | °C | |
| RTI Imp | 1.6mm | UL746 | 60.0 | °C |
| 3.0mm | UL746 | 60.0 | °C | |
| RTIStr | 1.6mm | UL746 | 60.0 | °C |
| 3.0mm | UL746 | 60.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC600932 | 3.8E+14 | ohms | |
| Volume resistivity | IEC600932 | >1.0E+13 | ohms·m | |
| Electrical strength | IEC60243-12 | 42 | KV/mm | |
| Relative permittivity | 1MHz | ASTM D1646 | 2.80 | |
| Dissipation factor | 1MHz | ASTM D1646 | 0.010 | |
| Arc resistance | ASTMD495 | PLC6 | ||
| Compared to the anti leakage trace index | CTI | UL746 | PLC0 | |
| Compared to the leakage trace index | ISO 2577 | 200 | ||
| High arc combustion index (HAI) | 1.6mm | UL746 | PLC1 | |
| 3.0mm | UL746 | PLC1 | ||
| High voltage arc ignition resistance index | PLC | UL746 | PLC6 | |
| Hot wire ignition (HWI) | 1.6mm | UL746 | PLC3 | |
| 3.0mm | UL746 | PLC3 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL94 | HB | |
| 3.0mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.