PC/ABS WONDERLOY® PC-365 TAIWAN CHIMEI
282
Unit Price:$2578 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 78MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance heat-resisting Flame retardant
- Application Areas:Automotive sector Electrical field Electronic field currency
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTMD792 | 1.13 | g/cm³ | |
| 23°C | ISO1183 | 1.13 | g/cm³ | |
| Melt mass flow rate | 260°C/5.0kg | ASTMD1238 | 20 | g/10min |
| 260°C/5.0kg | ISO1133 | 20 | g/10min | |
| SpiralFlow3. | 内部方法 | 30.0 | CM | |
| Shrinkage rate | MD | ASTMD955 | 0.40to0.60 | % |
| ISO2577 | 0.40to0.60 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Yield,23°C | ASTMD638 | 53.0 | Mpa |
| Yield | ISO527-2/50 | 54.0 | Mpa | |
| Break | ISO527-2/50 | 50.0 | Mpa | |
| Tensile strain | Break,23°C | ASTMD638 | 85 | % |
| elongation | Break | ISO527-2/50 | 120 | % |
| Bending modulus | 23°C | ASTMD790 | 2260 | Mpa |
| ISO178 | 2200 | Mpa | ||
| FlexuralStrength | 23°C | ASTMD790 | 78.5 | Mpa |
| Bending stress | ISO178 | 80.0 | Mpa | |
| Impact strength of simply supported beam gap | -30°C | ISO179 | 45 | kJ/m² |
| 23°C | ISO179 | 50 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C,3.18mm | ASTMD256 | 490 | J/m |
| 23°C,3.18mm | ASTMD256 | 540 | J/m | |
| -30°C | ISO180 | 45 | kJ/m² | |
| 23°C | ISO180 | 50 | kJ/m² | |
| Rockwell hardness | R-Sale,23°C | ASTMD785 | 115 | |
| R-Sale,23°C | ISO2039-2 | 115 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 106 | °C |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 115 | °C | |
| 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 102 | °C | |
| vicat softening point | -- | ASTMD152510 | 136 | °C |
| -- | ASTMD152511 | 125 | °C | |
| -- | ISO306/A50 | 138 | °C | |
| -- | ISO306/B50 | 127 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 8E-05 | cm/cm/°C |
| MD：23to55°C | ISO11359-2 | 8E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+16 | ohms | |
| Volume resistivity | IEC60093 | 1E+18 | ohms·cm | |
| Dielectric constant | 1MHz | IEC60250 | 3.10 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.