PC Makrolon® LED2245 000000 COVESTRO THAILAND
255
Unit Price:$4055 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 109.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:transparent High mobility Chemical resistance Flame retardant High temperature resistan
- Application Areas:Casters Electrical applications Automotive Applications lens Lighting applications Optical applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | 23°C | ISO1183 | 1.19 | g/cm³ |
| Apparent density | ISO60 | 0.66 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) | 300°C/1.2kg | ISO1133 | 34.0 | cm3/10min |
| Shrinkage rate | TD:2.00mm | ISO294-4 | 0.70 | % |
| MD:2.00mm | ISO294-4 | 0.65 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.30 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.12 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2/1 | 2350 | Mpa |
| tensile strength | Yield,23°C | ISO527-2/50 | 63.0 | Mpa |
| Break,23°C | ISO527-2/50 | 60.0 | Mpa | |
| elongation | Yield,23°C | ISO527-2/50 | 6.0 | % |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Suspended wall beam gap impact strength | -30°C,Complete Break | ISO7391 | 12 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 55 | kJ/m² | |
| Multi axis Instrumented Impact Energy | -30°C | ISO6603-2 | 60.0 | J |
| 23°C | ISO6603-2 | 55.0 | J | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO6603-2 | 5900 | N |
| 23°C | ISO6603-2 | 4900 | N | |
| Ball pressure hardness | ISO2039-1 | 115 | Mpa | |
| elongation | Break,23°C | ISO527-2/50 | 130 | % |
| Nominal tensile fracture strain | 23°C | ISO527-2/50 | >50 | % |
| Bending modulus | 23°C | ISO178 | 2350 | Mpa |
| bending strength | 3.5%Strain,23°C | ISO178 | 73.0 | Mpa |
| 23°C | ISO178 | 97.0 | Mpa | |
| Bending strain | 23°C | ISO178 | 7.1 | % |
| Impact strength of simply supported beam gap | -30°C,Complete Break | ISO7391 | 12 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 60 | kJ/m² | |
| Impact strength of simply supported beam without notch | -60°C | ISO179/1eU | NoBreak |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTIStr | 1.5mm | UL746 | 125 | °C |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 138 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 125 | °C | |
| Glass transition temperature | ISO11357-2 | 145 | °C | |
| vicat softening point | -- | ISO306/B50 | 145 | °C |
| -- | ISO306/B120 | 146 | °C | |
| Ball Pressure Test | 136°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
| Thermal conductivity coefficient | 23°C | ISO8302 | 0.20 | W/m/K |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| RTI Imp | 1.5mm | UL746 | 115 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+16 | ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 34 | KV/mm |
| Relative permittivity | 23°C,100Hz | IEC60250 | 3.10 | |
| 23°C,1MHz | IEC60250 | 3.00 | ||
| Dissipation factor | 23°C,100Hz | IEC60250 | 5E-04 | |
| 23°C,1MHz | IEC60250 | 9.5E-03 | ||
| Leakage Trace Index | SolutionA | IEC60112 | 250 | V |
| SolutionB | IEC60112 | 125 | V |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ISO489 | 1.584 | ||
| Light transmittance | 1000µm | ISO13468-2 | 90.0 | % |
| 2000µm | ISO13468-2 | 90.0 | % | |
| 3000µm | ISO13468-2 | >89.0 | % | |
| 4000µm | ISO13468-2 | >89.0 | % | |
| Haze | 3000µm | ISO14782 | <0.50 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 2.9mm,CL | UL94 | HB | |
| 0.75mm,CL | UL94 | V-2 | ||
| Burning wire flammability index | 1.0mm | IEC60695-2-12 | 850 | °C |
| 1.5mm | IEC60695-2-12 | 875 | °C | |
| 3.0mm | IEC60695-2-12 | 930 | °C | |
| Hot filament ignition temperature | 0.75mm | IEC60695-2-13 | 875 | °C |
| 1.5mm | IEC60695-2-13 | 875 | °C | |
| 3.0mm | IEC60695-2-13 | 900 | °C | |
| Extreme Oxygen Index | ISO4589-2 | 28 | % | |
| Burning rate - US-FMVSS | >1.00mm | ISO3795 | passed | |
| FlashIgnitionTemperature | ASTMD1929 | 480 | °C | |
| SelfIgnition | ASTMD1929 | 550 | °C |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortcut |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.