PC LEXAN™ LUX2114G-WH8B491 SABIC INNOVATIVE NANSHA
107
Unit Price:$4414 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 31MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Optics Weather resistance High mobility High impact resistance Aging resistance
- Application Areas:Lighting applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 特定体积 | ASTM D792 | 0.830 | cm³/g | |
| 熔体质量流动速率 | 300°C/1.2 kg | ASTM D1238 | 18 | g/10 min |
| 收缩率 - 流动 | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| 吸水率 | 24 hr | ASTM D570 | 0.15 | % |
| 平衡, 23°C | ASTM D570 | 0.35 | % | |
| 平衡, 100°C | ASTM D570 | 0.58 | % | |
| 室外适用性 | UL 746C | f2 |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 洛氏硬度 | M 级 | ASTM D785 | 70 | |
| R 级 | ASTM D785 | 118 | ||
| 拉伸强度 | 屈服 | ASTM D638 | 62.0 | Mpa |
| 断裂 | ASTM D638 | 65.0 | Mpa | |
| 伸长率 | 屈服 | ASTM D638 | 7.0 | % |
| 断裂 | ASTM D638 | 110 | % | |
| 弯曲模量 | 50.0 mm 跨距 | ASTM D790 | 2340 | Mpa |
| 弯曲强度 | 屈服, 50.0 mm 跨距 | ASTM D790 | 93.0 | Mpa |
| 泰伯耐磨性 | 1000 Cycles, 1000 g, CS-17 转轮 | ASTM D1044 | 10.0 | mg |
| 简支梁缺口冲击强度 | -30°C | ISO 179/1eA | 12 | kJ/m² |
| 23°C | ISO 179/1eA | 65 | kJ/m² | |
| 简支梁无缺口冲击强度 | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 | ||
| 无缺口悬臂梁冲击 | 23°C | ASTM D4812 | 3200 | J/m |
| -30°C 5 | ISO 180/1U | 无断裂 | ||
| 23°C 5 | ISO 180/1U | 无断裂 | ||
| 落锤冲击 | 23°C | ASTM D3029 | 169 | J |
| 拉伸冲击强度 | ASTM D1822 | 546 | kJ/m² |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 热变形温度 | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 137 | °C |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 132 | °C | |
| 维卡软化点 | ASTM D15257 | 154 | °C | |
| Ball Pressure Test | 123 到 127°C | IEC 60695-10-2 | 通过 | |
| 线形热膨胀系数 - 流动 | -40 到 95°C | ASTM E831 | 6.8E-5 | cm/cm/°C |
| 比热 | ASTM C351 | 1260 | J/kg/°C | |
| 导热系数 | ASTM C177 | 0.25 | W/m/K | |
| RTI Elec | UL 746 | 80.0 | °C | |
| RTI Imp | UL 746 | 80.0 | °C | |
| RTI | UL 746 | 80.0 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 体积电阻率 | ASTM D257 | > 1.0E+17 | ohms·cm | |
| 介电强度 | 3.20 mm, in Air | ASTM D149 | 15 | KV/mm |
| 介电常数 | 60 Hz | ASTM D150 | 3.17 | |
| 50 kHz | ASTM D150 | 3.17 | ||
| 1 MHz | ASTM D150 | 2.96 | ||
| 耗散因数 | 50 Hz | ASTM D150 | 9.0E-4 | |
| 60 Hz | ASTM D150 | 9.0E-4 | ||
| 1 MHz | ASTM D150 | 0.010 | ||
| 相比耐漏电起痕指数(CTI) | UL 746 | PLC 3 | ||
| 高电弧燃烧指数(HAI) | UL 746 | PLC 1 | ||
| 热丝引燃 (HWI) | UL 746 | PLC 3 |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥温度 | 120 | °C | ||
| 干燥时间 | 3.0 到 4.0 | hr | ||
| 建议的最大水分含量 | 0.020 | % | ||
| 建议注射量 | 40 到 60 | % | ||
| 料筒后部温度 | 260 到 280 | °C | ||
| 料筒中部温度 | 270 到 295 | °C | ||
| 料筒前部温度 | 280 到 305 | °C | ||
| 射嘴温度 | 275 到 300 | °C | ||
| 加工（熔体）温度 | 280 到 305 | °C | ||
| 模具温度 | 70 到 95 | °C | ||
| 背压 | 0.300 到 0.700 | Mpa | ||
| 螺杆转速 | 40 到 70 | rpm | ||
| 排气孔深度 | 0.025 到 0.076 | mm |
| 光学性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 折射率 | ASTM D542 | 1.586 |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL 阻燃等级 | 0.8 到 1.7 mm | UL 94 | V-2 | |
| 灼热丝易燃指数 | 0.75 mm | IEC 60695-2-12 | 750 | °C |
| 1.5 mm | IEC 60695-2-12 | 850 | °C | |
| 热灯丝点火温度 | 0.75 mm 9 | IEC 60695-2-13 | 875 | °C |
| 1.5 mm | IEC 60695-2-13 | 850 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.