PC Makrolon® 2807 020083 COVESTRO SHANGHAI
139
Unit Price:$3674 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Weather resistance UV resistance Medium viscosity
- Application Areas:Electrical field Electronic field Automotive sector Industrial components currency
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Apparent density | ISO60 | 0.66 | g/cm³ | |
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 10 | g/10min |
| Melt Volume-Flow Rate (MVR) | 300°C/1.2kg | ISO1133 | 9.00 | cm3/10min |
| Shrinkage rate | TD | ISO2577 | 0.60to0.80 | % |
| MD | ISO2577 | 0.60to0.80 | % | |
| TD:2.00mm3 | ISO294-4 | 0.70 | % | |
| MD:2.00mm3 | ISO294-4 | 0.65 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.30 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.12 | % | |
| density | 23°C | ISO1183 | 1.20 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap | -30°C,Complete Break | ISO7391 | 14 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 75 | kJ/m² | |
| Tensile modulus | 23°C | ISO527-2/1 | 2400 | Mpa |
| tensile strength | Yield,23°C | ISO527-2/50 | 66.0 | Mpa |
| Break,23°C | ISO527-2/50 | 70.0 | Mpa | |
| elongation | Yield,23°C | ISO527-2/50 | 6.1 | % |
| Break,23°C | ISO527-2/50 | 130 | % | |
| Nominal tensile fracture strain | 23°C | ISO527-2/50 | >50 | % |
| TensileCreepModule | 1hr | ISO899-1 | 2200 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 1900 | Mpa |
| Bending modulus | 23°C | ISO178 | 2400 | Mpa |
| bending strength | 3.5%Strain,23°C | ISO178 | 74.0 | Mpa |
| 23°C | ISO178 | 98.0 | Mpa | |
| Bending strain | 23°C | ISO178 | 7.0 | % |
| Impact strength of simply supported beam without notch | -60°C | ISO179/1eU | NoBreak | |
| -30°C | ISO179/1eU | NoBreak | ||
| 23°C | ISO179/1eU | NoBreak | ||
| Suspended wall beam gap impact strength | -30°C,Complete Break | ISO7391 | 15 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 70 | kJ/m² | |
| Multi axis Instrumented Impact Energy | -30°C | ISO6603-2 | 65.0 | J |
| 23°C | ISO6603-2 | 60.0 | J | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO6603-2 | 6300 | N |
| 23°C | ISO6603-2 | 5400 | N | |
| Ball pressure hardness | ISO2039-1 | 115 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 136 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 124 | °C | |
| Glass transition temperature | ISO11357-2 | 144 | °C | |
| vicat softening point | -- | ISO306/B50 | 143 | °C |
| -- | ISO306/B120 | 145 | °C | |
| Ball Pressure Test | 135°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
| Thermal conductivity coefficient | 23°C | ISO8302 | 0.20 | W/m/K |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| RTI Imp | 1.5mm | UL746 | 115 | °C |
| RTIStr | 1.5mm | UL746 | 125 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+16 | ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 34 | KV/mm |
| Relative permittivity | 23°C,100Hz | IEC60250 | 3.10 | |
| 23°C,1MHz | IEC60250 | 3.00 | ||
| Dissipation factor | 23°C,100Hz | IEC60250 | 5E-04 | |
| 23°C,1MHz | IEC60250 | 9E-03 | ||
| Leakage Trace Index | SolutionA | IEC60112 | 250 | V |
| SolutionB | IEC60112 | 125 | V |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| WaterVaporTransmission Rate | 23°C,85%RH,100µm | ISO15106-1 | 15 | g/m²/24hr |
| GasPermeation | CarbonDioxide:23°C,25.4µm | ISO2556 | 16900 | cm³/m²/bar/24hr |
| CarbonDioxide:23°C,100.0µm | ISO2556 | 3800 | cm³/m²/bar/24hr | |
| Nitrogen:23°C,25.4µm | ISO2556 | 510 | cm³/m²/bar/24hr | |
| Nitrogen:23°C,100.0µm | ISO2556 | 120 | cm³/m²/bar/24hr | |
| Oxygen:23°C,25.4µm | ISO2556 | 2760 | cm³/m²/bar/24hr | |
| Oxygen:23°C,100.0µm | ISO2556 | 650 | cm³/m²/bar/24hr |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ISO489 | 1.586 | ||
| Light transmittance | 1000µm | ISO13468-2 | 89.0 | % |
| 2000µm | ISO13468-2 | 89.0 | % | |
| 3000µm | ISO13468-2 | 88.0 | % | |
| 4000µm | ISO13468-2 | 87.0 | % | |
| Haze | 3000µm | ISO14782 | <0.80 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 2.5mm | UL94 | HB | |
| 0.75mm | UL94 | V-2 | ||
| Burning wire flammability index | 0.75mm | IEC60695-2-12 | 850 | °C |
| 1.5mm | IEC60695-2-12 | 850 | °C | |
| 3.0mm | IEC60695-2-12 | 930 | °C | |
| Hot filament ignition temperature | 0.75mm | IEC60695-2-13 | 875 | °C |
| 1.5mm | IEC60695-2-13 | 875 | °C | |
| 3.0mm | IEC60695-2-13 | 875 | °C | |
| Extreme Oxygen Index | ISO4589-2 | 28 | % | |
| Needle flame test | MethodK:3.00mm | IEC60695-11-5 | 0.2 | min |
| SelfIgnition | ASTMD1929 | 550 | °C | |
| ApplicationofFlamefromSmallBurner MethodKandF | 2.00mm | DIN53438-1,-3 | K1,F1 | |
| Burning rate - US-FMVSS | >1.00mm | ISO3795 | passed | |
| FlashIgnitionTemperature | ASTMD1929 | 480 | °C | |
| GlowWireTest | 1.50mm | EDFHN60E.02 | 750 | °C |
| 3.00mm | EDFHN60E.02 | 750 | °C | |
| Needle flame test | MethodF:1.50mm | IEC60695-11-5 | 1.0 | min |
| MethodF:2.00mm | IEC60695-11-5 | 1.0 | min | |
| MethodF:3.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodK:1.50mm | IEC60695-11-5 | 0.1 | min | |
| MethodK:2.00mm | IEC60695-11-5 | 0.1 | min |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ElectrolyticalCorrosion | 23°C | IEC60426 | A1 | |
| ISO Shortcut |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.