PC Makrolon® 2097 COVESTRO GERMANY
292
Unit Price:$9756 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:UV curing Good demolding performanc High temperature resistan High mobility
- Application Areas:Automotive sector Casters Medical supplies
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow : 2.00 mm | ISO 294-4 | 0.90 | % |
| 流量 : 2.00 mm | ISO 294-4 | 0.90 | % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.30 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.12 | % | |
| Melt Volume-Flow Rate (MVR) | 330°C/2.16 kg | ISO 1133 | 8.00 | cm3/10min |
| Melt mass flow rate | 330°C/2.16 kg | ISO 1133 | 8.0 | g/10 min |
| density | 23°C | ISO 1183 | 1.13 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | > 50 | % |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 | ||
| Ball pressure hardness | ISO 2039-1 | 130 | Mpa | |
| Tensile modulus | 23°C | ISO 527-2/1 | 2450 | Mpa |
| tensile strength | Yield, 23°C | ISO 527-2/50 | 76.0 | Mpa |
| elongation | Yield, 23°C | ISO 527-2/50 | 6.9 | % |
| Bending modulus | 23°C | ISO 178 | 2450 | Mpa |
| bending strength | 23°C | ISO 178 | 110 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | ISO 306/B120 | 202 | °C | |
| RTI | UL 746 | 150 | °C | |
| RTI Imp | UL 746 | 130 | °C | |
| RTI Elec | UL 746 | 150 | °C | |
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 191 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 172 | °C | |
| Linear coefficient of thermal expansion | Flow : 23 to 55°C | ISO 11359-2 | 6.5E-5 | cm/cm/°C |
| Across Flow : 23 to 55°C | ISO 11359-2 | 6.5E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | 1.0E+16 | ohms | |
| Volume resistivity | 23°C | IEC 60093 | 1.0E+17 | ohms·cm |
| Dissipation factor | 23°C, 100 Hz | IEC 60250 | 1.0E-3 | |
| 23°C, 1 MHz | IEC 60250 | 9.0E-3 | ||
| Dielectric strength | 23°C, 1.00 mm | IEC 60243-1 | 35 | KV/mm |
| Relative permittivity | 23°C, 100 Hz | IEC 60250 | 2.90 | |
| 23°C, 1 MHz | IEC 60250 | 2.80 | ||
| Leakage Trace Index | Solution A | IEC 60112 | 600 | V |
| Solution B | IEC 60112 | 100 | V |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Suggested maximum moisture content | < 0.020 | % | ||
| Processing (melt) temperature | 330 到 340 | °C | ||
| Mold temperature | 110 到 150 | °C | ||
| Suggested injection volume | 30 到 70 | % | ||
| Temperature at the rear of the barrel | 315 到 325 | °C | ||
| Temperature in the middle of the barrel | 320 到 330 | °C | ||
| Temperature at the front of the material cylinder | 325 到 335 | °C | ||
| Spray nozzle temperature | 315 到 340 | °C | ||
| Back pressure | 10.0 到 20.0 | Mpa | ||
| Exhaust hole depth | 0.025 到 0.050 | mm | ||
| Drying Temperature - Dry Air Dryer | 130 | °C | ||
| Drying time - Dry Air Dryer | 2.0 到 4.0 | hr |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Light transmittance | 1000 µm | ISO 13468-2 | 89.0 | % |
| Refractive index | ISO 489 | 1.566 | ||
| Electrolytical Corrosion | 23°C | IEC 60426 | A1 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning wire flammability index | IEC 60695-2-12 | 800 | °C | |
| UL flame retardant rating | 1.5 mm | UL 94 | HB | |
| Extreme Oxygen Index | ISO 4589-2 | 25 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.