PC Makrolon® APEC 2097 COVESTRO THAILAND
250
Unit Price:$10166 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 55MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:UV curing Good demolding performanc High temperature resistan High mobility
- Application Areas:Automotive sector Casters Nursing supplies Medical supplies
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | 23°C | ISO 1183 | 1.13 | g/cm³ |
| Melt mass flow rate | 330°C/2.16 kg | ISO 1133 | 8.0 | g/10 min |
| Melt Volume-Flow Rate (MVR) | 330°C/2.16 kg | ISO 1133 | 8.00 | cm3/10min |
| Shrinkage rate | Across Flow : 2.00 mm | ISO 294-4 | 0.90 | % |
| 流量 : 2.00 mm | ISO 294-4 | 0.90 | % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.30 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.12 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO 2039-1 | 130 | Mpa | |
| Tensile modulus | 23°C | ISO 527-2/1 | 2450 | Mpa |
| tensile strength | Yield, 23°C | ISO 527-2/50 | 76.0 | Mpa |
| elongation | Yield, 23°C | ISO 527-2/50 | 6.9 | % |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | > 50 | % |
| Bending modulus | 23°C | ISO 178 | 2450 | Mpa |
| bending strength | 23°C | ISO 178 | 110 | Mpa |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 191 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 172 | °C | |
| vicat softening point | ISO 306/B120 | 202 | °C | |
| Linear coefficient of thermal expansion | Flow : 23 to 55°C | ISO 11359-2 | 6.5E-5 | cm/cm/°C |
| Across Flow : 23 to 55°C | ISO 11359-2 | 6.5E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | 150 | °C | |
| RTI Imp | UL 746 | 130 | °C | |
| RTI | UL 746 | 150 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | 1.0E+16 | ohms | |
| Volume resistivity | 23°C | IEC 60093 | 1.0E+17 | ohms·cm |
| Dielectric strength | 23°C, 1.00 mm | IEC 60243-1 | 35 | KV/mm |
| Relative permittivity | 23°C, 100 Hz | IEC 60250 | 2.90 | |
| 23°C, 1 MHz | IEC 60250 | 2.80 | ||
| Dissipation factor | 23°C, 100 Hz | IEC 60250 | 1.0E-3 | |
| 23°C, 1 MHz | IEC 60250 | 9.0E-3 | ||
| Leakage Trace Index | Solution A | IEC 60112 | 600 | V |
| Solution B | IEC 60112 | 100 | V |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 130 | °C | ||
| Drying time - Dry Air Dryer | 2.0 到 4.0 | hr | ||
| Suggested maximum moisture content | < 0.020 | % | ||
| Suggested injection volume | 30 到 70 | % | ||
| Temperature at the rear of the barrel | 315 到 325 | °C | ||
| Temperature in the middle of the barrel | 320 到 330 | °C | ||
| Temperature at the front of the material cylinder | 325 到 335 | °C | ||
| Spray nozzle temperature | 315 到 340 | °C | ||
| Processing (melt) temperature | 330 到 340 | °C | ||
| Mold temperature | 110 到 150 | °C | ||
| Back pressure | 10.0 到 20.0 | Mpa | ||
| Exhaust hole depth | 0.025 到 0.050 | mm |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ISO 489 | 1.566 | ||
| Light transmittance | 1000 µm | ISO 13468-2 | 89.0 | % |
| Electrolytical Corrosion | 23°C | IEC 60426 | A1 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB | |
| Burning wire flammability index | IEC 60695-2-12 | 800 | °C | |
| Extreme Oxygen Index | ISO 4589-2 | 25 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.