PC Makrolon® 9417 700394 COVESTRO SHANGHAI
190
Unit Price:$3367 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:high viscosity High temperature resistan Filler: Glass fiber reinf 10% filler by weight 10% filler by weight
- Application Areas:Electronic and electrical Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO2577 | 0.40to0.60 | % |
| MD | ISO2577 | 0.40to0.60 | % | |
| TD:2.00mm3 | ISO294-4 | 0.45 | % | |
| MD:2.00mm3 | ISO294-4 | 0.60 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.26 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.10 | % | |
| Melt Volume-Flow Rate (MVR) | 300°C/1.2kg | ISO1133 | 6.00 | cm3/10min |
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 7.0 | g/10min |
| Apparent density | ISO60 | 0.64 | g/cm³ | |
| density | 23°C | ISO1183 | 1.27 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| NotchedIzodImpactStrength | 23°C,CompleteBreak | ISO7391 | 10 | kJ/m² |
| CharpyNotchedImpactStrength | 23°C,CompleteBreak | ISO7391 | 10 | kJ/m² |
| Bending strain | 23°C | ISO178 | 5.8 | % |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO6603-2 | 3700 | N |
| 23°C | ISO6603-2 | 4000 | N | |
| Impact strength of simply supported beam without notch | -60°C,CompleteBreak | ISO179/1eU | 100 | kJ/m² |
| -30°C,Complete Break | ISO179/1eU | 120 | kJ/m² | |
| 23°C,Complete Break | ISO179/1eU | 150 | kJ/m² | |
| Ball pressure hardness | ISO2039-1 | 128 | Mpa | |
| TensileCreepModule | 1hr | ISO899-1 | 3600 | Mpa |
| Multi axis Instrumented Impact Energy | 23°C | ISO6603-2 | 25.0 | J |
| -30°C | ISO6603-2 | 15.0 | J | |
| Tensile creep modulus | 1000hr | ISO899-1 | 2900 | Mpa |
| Tensile modulus | 23°C | ISO527-2/1 | 3800 | Mpa |
| tensile strength | Yield,23°C | ISO527-2/5 | 64.0 | Mpa |
| Break,23°C | ISO527-2/5 | 45.0 | Mpa | |
| elongation | Yield,23°C | ISO527-2/5 | 4.6 | % |
| Break,23°C | ISO527-2/5 | 15 | % | |
| Bending modulus | 23°C | ISO178 | 3600 | Mpa |
| bending strength | 3.5%Strain,23°C | ISO178 | 95.0 | Mpa |
| 23°C | ISO178 | 105 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | -- | ISO306/B50 | 143 | °C |
| -- | ISO306/B120 | 144 | °C | |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| RTIStr | 1.5mm | UL746 | 125 | °C |
| RTI Imp | 1.5mm | UL746 | 115 | °C |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 4E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 141 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 135 | °C | |
| Ball Pressure Test | 136°C | IEC60695-10-2 | Pass | |
| Thermal conductivity coefficient | 23°C | ISO8302 | 0.22 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative permittivity | 23°C,100Hz | IEC60250 | 3.20 | |
| 23°C,1MHz | IEC60250 | 3.20 | ||
| Leakage Trace Index | SolutionA | IEC60112 | 175 | V |
| SolutionB | IEC60112 | 125 | V | |
| Dissipation factor | 23°C,100Hz | IEC60250 | 1E-03 | |
| 23°C,1MHz | IEC60250 | 9E-03 | ||
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 36 | KV/mm |
| Surface resistivity | IEC60093 | 1E+16 | ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 | |
| 3.0mm,NC,BK,GY | UL94 | 5VA | ||
| 6.0mm | UL94 | 5VA | ||
| Burning wire flammability index | 0.75mm | IEC60695-2-12 | 960 | °C |
| 1.5mm | IEC60695-2-12 | 960 | °C | |
| 3.0mm | IEC60695-2-12 | 960 | °C | |
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 825 | °C |
| 1.5mm | IEC60695-2-13 | 900 | °C | |
| 3.0mm | IEC60695-2-13 | 900 | °C | |
| Extreme Oxygen Index | ISO4589-2 | 35 | % | |
| ApplicationofFlamefromSmallBurner MethodKandF | 2.00mm | DIN53438-1,-3 | K1,F1 | |
| Burning rate - US-FMVSS | >1.00mm | ISO3795 | passed | |
| FlashIgnitionTemperature | ASTMD1929 | 470 | °C | |
| SelfIgnition | ASTMD1929 | 550 | °C |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ElectrolyticalCorrosion | 23°C | IEC60426 | A1 | |
| ISO Shortcut |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.