PC TARFLON™ URC2501 IDEMITSU JAPAN
240
Unit Price:$6082 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant High reflectivity
- Application Areas:Lighting diffuser
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.38 | ||
| Melt mass flow rate | ASTM D1238/ISO 1133 | 35 cm3/10min(300℃/1.2kg ) | g/10min | |
| Melt Volume-Flow Rate (MVR) | 300°C/1.2kg | ISO1133 | 35.0 | cm3/10min |
| Shrinkage rate | TD:2.00mm | 内部方法 | 0.50to0.60 | % |
| MD:2.00mm | 内部方法 | 0.50to0.60 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | Yield | ISO527-2 | 50.0 | Mpa |
| Nominal tensile fracture strain | ISO527-2 | 70 | % | |
| Bending modulus | ISO178 | 2200 | Mpa | |
| bending strength | ISO178 | 80.0 | Mpa | |
| Tensile yield stress | ISO 527-1 | 50 | Mpa | |
| elongation | Break | ISO 527-1 | 70 | % |
| Tensile modulus of elasticity | ISO 527-1 | 2100 | Mpa | |
| bending strength | ISO 178 | 80 | Mpa | |
| Flexural modulus of elasticity | ISO 178 | 2200 | Mpa | |
| Gap impact strength | ISO 176 | 30 | k/Jm2 | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 30 | kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | tB 70 | % | |
| tensile strength | ASTM D638/ISO 527 | 50 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 2.2(GPa) | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 80 | kg/cm²(MPa)[Lb/in²] |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | V0/1.0mm | ||
| RTI Imp | UL746 | 80.0 | °C | |
| RTIStr | UL746 | 80.0 | °C | |
| Hot deformation temperature | 1.8MPa | ISO 75-1-2 | 125 | °C |
| 0.46MPa | ISO 75-1-2 | 136 | °C | |
| Flame retardant grade | 1.0mm | UL94 | V-0 | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 136 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 125 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| RTIElec | UL746 | 80.0 | °C |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Light transmittance | 1000µm | ISO13468-1 | 0.1 | % |
| Huangdu Index | 9.0 | YI | ||
| Refractive index | D65 type,10 | ISO 13468-1 | 97.5 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 1.0mm,NC | UL94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortcut | >PC-MD20< |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| MVR | ISO 1133 | 32 | cm3/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.