PC Makrolon® RX1805 COVESTRO THAILAND
238
Unit Price:$7137 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 32MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:transparent
- Application Areas:Medical supplies
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD:2.00mm3 | ISO294-4 | 0.70 | % |
| MD:2.00mm3 | ISO294-4 | 0.70 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.30 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.12 | % | |
| density | 23°C | ISO1183 | 1.20 | g/cm³ |
| Apparent density | ISO60 | 0.66 | g/cm³ | |
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 6.5 | g/10min |
| Melt Volume-Flow Rate (MVR) | 300°C/1.2kg | ISO1133 | 6.00 | cm3/10min |
| Shrinkage rate | TD | ISO2577 | 0.60to0.80 | % |
| MD | ISO2577 | 0.60to0.80 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2/1 | 2400 | Mpa |
| tensile strength | Yield,23°C | ISO527-2/50 | 67.0 | Mpa |
| Break,23°C | ISO527-2/50 | 75.0 | Mpa | |
| elongation | Yield,23°C | ISO527-2/50 | 6.3 | % |
| Break,23°C | ISO527-2/50 | 130 | % | |
| Nominal tensile fracture strain | 23°C | ISO527-2/50 | >50 | % |
| Bending modulus | 23°C | ISO178 | 2400 | Mpa |
| bending strength | 3.5%Strain,23°C | ISO178 | 73.0 | Mpa |
| 23°C | ISO178 | 98.0 | Mpa | |
| Bending strain | 23°C | ISO178 | 7.1 | % |
| Impact strength of simply supported beam gap | -30°C,Complete Break | ISO7391 | 16 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 80 | kJ/m² | |
| Impact strength of simply supported beam without notch | -60°C | ISO179/1eU | NoBreak | |
| -30°C | ISO179/1eU | NoBreak | ||
| 23°C | ISO179/1eU | NoBreak | ||
| Suspended wall beam gap impact strength | -30°C,Complete Break | ISO7391 | 15 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 70 | kJ/m² | |
| Multi axis Instrumented Impact Energy | -30°C | ISO6603-2 | 70.0 | J |
| 23°C | ISO6603-2 | 65.0 | J | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO6603-2 | 6600 | N |
| 23°C | ISO6603-2 | 5700 | N | |
| Ball pressure hardness | ISO2039-1 | 114 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 138 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 126 | °C | |
| Glass transition temperature | ISO11357-2 | 145 | °C | |
| vicat softening point | -- | ISO306/B50 | 144 | °C |
| -- | ISO306/B120 | 145 | °C | |
| Ball Pressure Test | 135°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
| Thermal conductivity coefficient | 23°C | ISO8302 | 0.20 | W/m/K |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | ISO4589-2 | 27 | % | |
| FlashIgnitionTemperature | ASTMD1929 | 480 | °C | |
| SelfIgnition | ASTMD1929 | 550 | °C |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortcut |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.