PC LEXAN™ PK2870 SABIC INNOVATIVE US
133
Unit Price:$2286 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance wear resistant high viscosity
- Application Areas:chip
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume-Flow Rate (MVR) | 300°C/1.2kg | ISO1133 | 2.00 | cm3/10min |
| 300°C/2.16kg | ISO1133 | 4.00 | cm3/10min | |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 0.35 | % |
| Equilibrium,23°C | ASTMD570 | 0.35 | % | |
| Equilibrium,100°C | ASTMD570 | 0.58 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % | |
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 2.5 | g/10min |
| density | ASTMD792 | 1.20 | g/cm³ | |
| ISO1183 | 1.20 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTMD4812 | NoBreak | |
| -30°C | ASTMD4812 | NoBreak | ||
| -30°C | ASTMD256 | 150 | J/m | |
| 23°C | ASTMD256 | 750 | J/m | |
| Falling hammer impact | 23°C | ASTMD3029 | 170 | J |
| Unscented Izod Impact Strength | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Bending strength 5, | ISO178 | 95.0 | Mpa | |
| Impact strength of simply supported beam gap | -30°C | ISO179/1eA | 50 | kJ/m² |
| 23°C | ISO179/1eA | 70 | kJ/m² | |
| The impact strength of a simply supported beam without a notch is | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Suspended wall beam gap impact strength | -30°C | ISO180/1A | 55 | kJ/m² |
| 23°C | ISO180/1A | 75 | kJ/m² | |
| Tensile modulus | ASTMD638 | 2350 | Mpa | |
| ISO527-2/1 | 2350 | Mpa | ||
| tensile strength | Yield | ASTMD638 | 62.0 | Mpa |
| Yield | ISO527-2/50 | 65.0 | Mpa | |
| Break | ASTMD638 | 65.0 | Mpa | |
| Break | ISO527-2/50 | 70.0 | Mpa | |
| elongation | Yield | ASTMD638 | 7.0 | % |
| Yield | ISO527-2/50 | 7.0 | % | |
| Break | ASTMD638 | >70 | % | |
| Break | ISO527-2/50 | >70 | % | |
| Rockwell hardness | R-Scale | ISO2039-2 | 120 | |
| Bending modulus | 50.0mmSpan | ASTMD790 | 2300 | Mpa |
| ISO178 | 2300 | Mpa | ||
| bending strength | Yield,50.0mmSpan | ASTMD790 | 93.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | -- | ISO306/B50 | 149 | °C |
| -- | ISO306/B120 | 150 | °C | |
| ASTMD152510 | 150 | °C | ||
| Ball Pressure Test | 125°C | IEC60695-10-2 | Pass | |
| specific heat | ASTMC351 | 1250 | J/kg/°C | |
| thermal conductivity | ASTMC177 | 0.20 | W/m/K | |
| ISO8302 | 0.20 | W/m/K | ||
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 145 | °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 145 | °C | |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 130 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 130 | °C | |
| Linear coefficient of thermal expansion | MD：-40to95°C | ASTME831 | 7E-05 | cm/cm/°C |
| MD：23to80°C | ISO11359-2 | 7E-05 | cm/cm/°C |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Haze | 2540µm | ASTMD1003 | <0.80 | % |
| Light transmittance | 2540µm | ASTMD1003 | 88.0 | % |
| Refractive index | ISO489 | 1.586 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.