POM DURACON® GH-25 JAPAN POLYPLASTIC
282
Unit Price:$4915 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:high strength High rigidity Glass fiber reinforced Filler: Glass fiber reinf 25% filler by weight
- Application Areas:Bottle cap Electronic and electrical
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 190°C/2.16kg | ISO1133 | 2.5 | g/10min |
| Melt Volume-Flow Rate (MVR) | 190°C/2.16kg | ISO1133 | 1.80 | cm3/10min |
| Shrinkage rate | TD:2.00mm | ISO294-4 | 0.90 | % |
| MD:2.00mm | ISO294-4 | 0.60 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.70 | % |
| density | ISO1183 | 1.59 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| friction coefficient | Dynamic2 | JISK7218 | 0.37 | |
| Steel - Dynamic3 | JISK7218 | 0.60 | ||
| Wear factor | 0.060MPa,0.15m/sec4 | JISK7218 | 300 | 10^-8mm³/N·m |
| 0.49MPa,0.30m/sec5 | JISK7218 | 400 | 10^-8mm³/N·m | |
| 0.49MPa,0.30m/sec6 | JISK7218 | 8000 | 10^-8mm³/N·m | |
| 0.060MPa,0.15m/sec7 | JISK7218 | 10000 | 10^-8mm³/N·m | |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 8.0 | kJ/m² |
| Rockwell hardness | M-Scale | ISO2039-2 | 90 | |
| Tensile modulus | ISO527-2 | 8500 | Mpa | |
| tensile strength | ISO527-2 | 136 | Mpa | |
| elongation | Break | ISO527-2 | 2.8 | % |
| Bending modulus | ISO178 | 7900 | Mpa | |
| bending strength | ISO178 | 200 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 9E-05 | cm/cm/°C |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 162 | °C |
| Linear coefficient of thermal expansion | MD：23to55°C | 内部方法 | 3E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 9E+15 | ohms | |
| Volume resistivity | IEC60093 | 5E+13 | ohms·cm | |
| Dielectric strength | 3.00mm | IEC60243-1 | 24 | KV/mm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ColourNumber | CF3500/CD3501 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.