PMMA Altuglas® V825T-101 ARKEMA ITALY
236
Unit Price:$7975 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:transparent wear resistant High temperature resistan
- Application Areas:Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 230°C/3.8 kg | ISO 1133 | 2.8 | g/10 min |
| Shrinkage rate - flow | ASTM D955 | 0.20 到 0.60 | % | |
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 0.30 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ASTM D785 | 97 | |
| tensile strength | Yield, 23°C | ISO 527-2 | 70.0 | Mpa |
| elongation | Break, 23°C | ISO 527-2 | 6.0 | % |
| Bending modulus | 23°C | ISO 178 | 3300 | Mpa |
| bending strength | 23°C | ISO 178 | 103 | Mpa |
| Compressive stress | 23°C | ISO 604 | 117 | Mpa |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/2U | 11 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 103 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 100 | °C | |
| vicat softening point | ISO 306/B | 108 | °C | |
| Linear coefficient of thermal expansion - flow | -30 to 23°C | ASTM D696 | 6.5E-5 | cm/cm/°C |
| specific heat | 2090 | J/kg/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTM D257 | > 1.0E+14 | ohms | |
| Volume resistivity | ASTM D257 | > 1.0E+15 | ohms·cm | |
| Dielectric strength | ASTM D149 | 20 | KV/mm | |
| Dielectric constant | 60 Hz | ASTM D150 | 3.70 | |
| Dissipation factor | 1 MHz | ASTM D150 | 0.040 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 85 到 90 | °C | ||
| drying time | 2.0 到 4.0 | hr | ||
| Processing (melt) temperature | 230 到 250 | °C | ||
| Mold temperature | 80 到 90 | °C |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ISO 489 | 1.490 | ||
| Light transmittance | ASTM D1003 | 92.0 | % | |
| Haze | ASTM D1003 | 0.50 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.