PA66 Vydyne® R513H BK ASCEND USA
152
Unit Price:$4166 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 13MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Lubricity Thermal stability Oil resistant Antichemical High mobility Antisolvent high strength High rigidity
- Application Areas:Electrical appliances Laptop case Parts box Lighting applications switch Electrical enclosure Electrical components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | 横向流量 : 23°C, 2.00 mm | ISO 294-4 | 1.0 | % |
| 流量 : 23°C, 2.00 mm | ISO 294-4 | 0.50 | % | |
| 吸水率 | 24 hr, 23°C | ISO 62 | 1.0 | % |
| 平衡, 23°C, 50% RH | ISO 62 | 2.2 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 拉伸模量 | 23°C | ISO 527-2 | 6200 | Mpa |
| 拉伸强度 | 断裂, 23°C | ISO 527-2 | 115 | Mpa |
| 伸长率 | 断裂, 23°C | ISO 527-2 | 3.0 | % |
| 弯曲模量 | 23°C | ISO 178 | 5200 | Mpa |
| 弯曲强度 | 23°C | ISO 178 | 165 | Mpa |
| 泊松比 | ISO 527-2 | 0.40 | ||
| 简支梁无缺口冲击强度 | -30°C | ISO 179 | 31 | kJ/m² |
| 23°C | ISO 179 | 38 | kJ/m² |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 热变形温度 | 0.45 MPa, 未退火 | ISO 75-2/B | 258 | °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 240 | °C | |
| 熔融温度 | ISO 11357-3 | 260 | °C | |
| 线性热膨胀系数 | 流动 : 23 到 55°C, 2.00 mm | ISO 11359-2 | 3.0E-5 | cm/cm/°C |
| 横向 : 23 到 55°C, 2.00 mm | ISO 11359-2 | 1.1E-4 | cm/cm/°C | |
| RTI Elec | 0.75 mm | UL 746 | 140 | °C |
| 1.5 mm | UL 746 | 140 | °C | |
| 3.0 mm | UL 746 | 140 | °C | |
| RTI Imp | 0.75 mm | UL 746 | 120 | °C |
| 1.5 mm | UL 746 | 120 | °C | |
| 3.0 mm | UL 746 | 120 | °C | |
| RTI | 0.75 mm | UL 746 | 125 | °C |
| 1.5 mm | UL 746 | 140 | °C | |
| 3.0 mm | UL 746 | 140 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 体积电阻率 | 0.750 mm | IEC 60093 | 1.0E+13 | ohms·cm |
| 介电强度 | 1.00 mm | IEC 60243 | 20 | KV/mm |
| 耐电弧性 | 3.00 mm | ASTM D495 | PLC 6 | |
| 漏电起痕指数 | 3.00 mm | IEC 60112 | 250 到 399 | V |
| 高电弧燃烧指数(HAI) | 0.75 mm | UL 746 | PLC 0 | |
| 1.5 mm | UL 746 | PLC 0 | ||
| 3.0 mm | UL 746 | PLC 0 | ||
| 高电压电弧起痕速率 (HVTR) | UL 746 | PLC 1 | ||
| 热丝引燃 (HWI) | 0.75 mm | UL 746 | PLC 4 | |
| 1.5 mm | UL 746 | PLC 3 | ||
| 3.0 mm | UL 746 | PLC 4 |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥温度 | 80 | °C | ||
| 干燥时间 | 4.0 | hr | ||
| 建议的最大回制料比例 | 25 | % | ||
| 料筒后部温度 | 280 到 310 | °C | ||
| 料筒中部温度 | 280 到 310 | °C | ||
| 料筒前部温度 | 280 到 310 | °C | ||
| 射嘴温度 | 280 到 310 | °C | ||
| 加工（熔体）温度 | 285 到 305 | °C | ||
| 模具温度 | 65 到 95 | °C |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL 阻燃等级 | 0.75 mm | UL 94 | HB | |
| 1.5 mm | UL 94 | HB | ||
| 3.0 mm | UL 94 | HB | ||
| 灼热丝易燃指数 | 0.75 mm | IEC 60695-2-12 | 675 | °C |
| 1.5 mm | IEC 60695-2-12 | 675 | °C | |
| 3.0 mm | IEC 60695-2-12 | 675 | °C | |
| 热灯丝点火温度 | 0.75 mm | IEC 60695-2-13 | 700 | °C |
| 1.5 mm | IEC 60695-2-13 | 700 | °C | |
| 3.0 mm | IEC 60695-2-13 | 700 | °C | |
| 极限氧指数 | ISO 4589-2 | 25 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.